Abstract:We evaluated dry reforming of methane in a tubular fixed-bed reactor at various reaction temperatures from 923 to 973 K using different reactant compositions over 10 % Ni/Al2O3 catalyst prepared by a wet impregnation method. Both NiO and NiAl2O4 phases were formed on the catalyst surface during calcination, and the 10 % Ni/Al2O3 catalyst possessed high surface area of 106.36 m2 g−1 with fine metal dispersion. The low activation energy observed for formation of NiAl2O4 phase during calcination indicated strong interaction between the NiO form and the γ-Al2O3 support. The NiO phase was completely reduced to metallic Ni0 form via H2 reduction. The conversions of CO2 and CH4 increased noticeably with increasing CO2 partial pressure, and the H2/CO ratio was always below unity, regardless of reaction conditions. The yield of H2 was enhanced with growing CO2 partial pressure, approaching a highest value of about 70 %. The heterogeneous nature of the deposited carbon was evident from the coexistence of carbon nanofibers and graphitic carbon. In addition, the amount of filamentous carbon appeared to be slightly less than that of graphitic carbon. However, these deposited carbons were completely removed by O2 at below 900 K during temperature-programmed oxidation.

Syngas Production Via Combined Oxy-Co2 Reforming of Methane over Gd2O3-modified Ni/SiO2 Catalysts in a Fluidized-Bed Reactor

Catalytic conversion of CH4 and CO2 to synthesis gas on Ni/SiO2 catalysts containing Gd2O3 promoter

Combination of CO2 Reforming and Partial Oxidation of Methane over Ni/BaO-SiO2 Catalysts to Produce Low H2/CO Ratio Syngas Using a Fluidized Bed Reactor

Syngas Production from Reforming of Methane with Co2 and O-2 over Ni/Sro-Sio2 Catalysts in A Fluidized Bed Reactor

Combined Carbon Dioxide Reforming and Partial Oxidation of Methane to Syngas over Ni−La2O3/SiO2 Catalysts in a Fluidized-Bed Reactor

Catalytic conversion of methane and CO2 to synthesis gas over a La2O3-modified SiO2 supported Ni catalyst in fluidized-bed reactor

Combined Carbon Dioxide Reforming and Partial Oxidation of Methane to Syngas over Ni−La<sub>2</sub>O<sub>3</sub>/SiO<sub>2</sub>Catalysts in a Fluidized-Bed Reactor

Reforming of CH4with CO2and O2to Produce Syngas over CaO Modified Ni/SiO2catalysts in a Fluidized Bed Reactor

Reforming of CH 4 with CO 2 and O 2 to produce syngas over CaO modified Ni/SiO 2 catalysts in a fluidized bed reactor

Combined Catalytic Partial Oxidation and CO2 Reforming of Methane over ZrO2-modified Ni/SiO2 Catalysts Using Fluidized-Bed Reactor

Catalytic Performance of Ni/CaO-SiO2 for Converting Methane to Syngas in A Fluidized Bed Reactor

Catalytic Performance of Ni/SiO2 in Converting Methane to Syngas Using Fluidized Bed Reactor

Production of Syngas Via Partial Oxidation and CO2Reforming of Coke Oven Gas over a Ni Catalyst

Erratum To: Effect of Gd2O3 over Ni/SiO2 on Syngas Production Via Methane Autothermal Reforming

Production of Syngas Via Autothermal Reforming of Methane in a Fluidized-Bed Reactor over the Combined CeO2–ZrO2/SiO2 Supported Ni Catalysts

Study on Reforming of CH4 and C3H8 with CO2 and O2 to Syngas in a Fluidized Bed Reactor

Ni/SiO<sub>2</sub>Catalyst Prepared with Nickel Nitrate Precursor for Combination of CO<sub>2</sub>Reforming and Partial Oxidation of Methane: Characterization and Deactivation Mechanism Investigation

Combination of CO 2 reforming and partial oxidation of CH 4 over Ni/Al 2 O 3 catalysts using fluidized bed reactor

Carbon Dioxide Reforming of Methane over Ni Supported SiO2: Influence of the Preparation Method on the Resulting Structural Properties and Catalytic Activity

Ni/SiO2 Catalyst Prepared with Nickel Nitrate Precursor for Combination of CO2 Reforming and Partial Oxidation of Methane: Characterization and Deactivation Mechanism Investigation

Syngas production from methane dry reforming over Ni/Al2O3 catalyst