Abstract:In this paper, We prepared two groups of the glasses, the first group is Ge x As 20 Se 80-x with x from 5 % to 32.5 %, the second group is Ge x Sb 20 Se 80-x with x from 5 % to 25 %, using the conventional melt-quench method, and investigated the effect of the elemental substitution of As by Sb on the threshold behaviors in Ge x As(Sb) 20 Se 80-x glasses. We aimed to understand that,to which degree the topological model and chemical order model can explain the correlation between the physical properties and glass compositions, and how the chemical composition can affect the transition threshold in the glasses. Glass transition temperature was measured by the differential scanning calorimeter (Mettler-Toledo, DSC1) with different scanning rates from 5 K/min to 30 K/min under a uniform nitrogen gas flow of 50 mL/min, the density of the glasses was measured by a Mettler H20 balance with a MgO crystal used as a reference. Samples from each glass composition were weighed five times and the average density was recorded, the refractive index of the glass at 1.5 um was measured by a Metricon Model 2010 prism coupler. Raman spectra were measured from a T64000 Jobin-Yvon-Horiba micro-Raman spectrometer equipped with a liquid-nitrogen-cooled CCD detector. The 830 nm laser line was used as an excitation source, and the laser power was kept as small as possible to avoid any photo-induced effects. The resolution of the spectrometer was about 0.5 cm -1 . The result from systematic measurements of these physical parameters shows that, while the transition thresholds at MCN=2.4 and 2.67 were verified in the Ge-As-Se glasses with ideal covalent network, these two transitions represent the covalent network structure inside the glass from an under-constrained “floppy” network to an over-constrained “rigid” phase and from the two-dimensional to the three-dimensional “stressed rigid” phase respectively. However, when As is substituted by Sb, the Ge x Sb 20 Se 80-x glass with non-ideal covalent network will change of the transition thresholds, which changes to the chemically stoichiometric composition. We further deconvolved Raman scattering spectra into different structural units and the change of their respective intensity showed the same behavior, and this was ascribed to the chemical effect induced by a large difference of the atomic radius between As and Sb, and a relatively strong ionic feature of the element Sb.

Relationship Between the Average Coordination Number and Properties of Chalconitride Glasses

Role of Nitrogen in the Crystallization of Silicon Nitride-Doped Chalcogenide Glasses

Properties of Ge-Si-As-Se-Te-N Chalconitride Glasses As Infrared Transmitting Materials

Properties of Dy3+‐Doped Ge–As–Ga–Se Chalcogenide Glasses

Relationship Between Density and Structure of the Chalconitride Glasses

Mutual effects of Ag doping and non-stoichiometric glass forming units on the structural, thermal, and electrical properties of Ag30+xAs28-xSe21Te21 chalcogenide glasses

Properties of Chalcohalide Glasses in the Ge-As-Se-Te-I System

Raman Spectra of Ge-Si-As-Se-Te-N Chalconitride Glasses

Effect of the elemental substitution on threshold behaviours in Ge-As(Sb)-Se glasses

Nanophase Separation and Effects on Properties of Ge–As–Se Chalcogenide Glasses

Effects of the Se Substitution for Te on the Structure and Properties of Glasses in the Ag30As28(SexTe100-x)42 System

Formation and Properties of Chalcogenide Glasses in the GeSe2-As2Se3-CdSe System

Effect of Iodine (I-2) on Structural, Thermal and Optical Properties of Ge-Sb-S Chalcohalide Host Glasses and Ones Doped with Dy

Glass forming region and optical properties of chalcogenide glasses within a gallium-tin-selenium ternary system

Effects of Ag Addition on Properties and Structure of Ge–Ga–Se–AgI Chalcohalide Glasses

Understanding Aging in Chalcogenide Glass Thin Films Using Precision Resonant Cavity Refractometry

Effect of Annealing Conditions on the Physio-Chemical Properties of Spin-Coated As2se3 Chalcogenide Glass Films

Synthesis and Characterization of Chloro-Sulphide Glass-Ceramics Containing Neodymium(Iii) Ions

Composition dependence of the physical and acousto-optic properties of transparent Ge–As–S chalcogenide glasses

Iodine-doped Ge-As-Se glasses with high purity and low dispersion

Properties of the GeS2-Ga2S3-CsCl-GeO 2 oxy-chalcohalide glasses