Abstract:In this work, we report the sensitivity of structural, thermal, and electrical properties of Ag30+xAs28-xSe21Te21 (x = 2, 4, 6, 8, 10) chalcogenide glasses to the relative abundance of Ag and As in the compositions. The results show non-linear variation of glass density with linear increase in Ag (or decrease in As), implying structural change at 38 at.% Ag (or 20 at.% As). This structure change was further evident from differential scanning calorimetry (DSC) and Raman analyses, which show distinct characteristic temperatures (Tg, Tx, and Tp) and bonding type with increasing Ag content (decreasing As content). Specifically, at high Ag content beyond 38 at.% (As below 20 at.%), two additional exothermic peaks appear in DSC curves, and a strong As–Se bonding peak appears in Raman. The structural change is closely related to the variation of glass conductivity in a complex way, which first decreases with increasing Ag content, from 1.14 × 10−6 S cm−1 at 32 at.% Ag to 2.88 × 10−7 S cm−1 at 36 at.% Ag, but then with further increase in Ag, conductivity increases rapidly and reaches the maximum of 5.20 × 10−6 S cm−1 at the maximum Ag content 40 at.%. The abnormal change in conductivity is interpreted as due to the mutual effects of Ag doping as well as the degree of deviation from stoichiometry of the glass forming units. The impedance spectra identify little ionic contribution to the total conductivity which is supported from Raman spectra of the glasses and XRD analyses of the samples after thermal crystallization, both showing evidences of the presence of lone pair electrons of the chalcogen atoms. This work highlights the importance of compositional adjustment for the modification of physical properties in chalcogenide glasses, and provides a scientific basis for potential applications of such glasses in electronic devices.

Properties of Chalcohalide Glasses in the Ge-As-Se-Te-I System

Chalcogenide Coatings of Ge_15Sb_20S_65 and Te_20As_30Se_50

Properties of Ge-Si-As-Se-Te-N Chalconitride Glasses As Infrared Transmitting Materials

Formation and Structure of Chalcohalide Glasses in the As2Se3-AsTe-CuI System

Effects of Ag Addition on Properties and Structure of Ge–Ga–Se–AgI Chalcohalide Glasses

Properties of Dy3+‐Doped Ge–As–Ga–Se Chalcogenide Glasses

Formation and Properties of Chalcogenide Glasses in the GeSe2-As2Se3-CdSe System

Mutual effects of Ag doping and non-stoichiometric glass forming units on the structural, thermal, and electrical properties of Ag30+xAs28-xSe21Te21 chalcogenide glasses

Glass forming region and optical properties of chalcogenide glasses within a gallium-tin-selenium ternary system

Glass formation, density, microhardness, and optical properties of As–Si–Te chalcogenide alloys

Iodine-doped Ge-As-Se glasses with high purity and low dispersion

Thermal properties of chalcogenide glasses in the GeSe2–As2Se3–CdSe system

Thermal, structural, and conductivity properties of As14Sb26S(60−x)–(AgI)x chalcogenide glasses

Optical Properties and Local Structure of Dy3+-doped Chalcogenide and Chalcohalide Glasses

Optical properties and structural rigidity of [(GeSe2)75(Sb2Se3)25]100−xTex chalcogenide glasses for potential applications in infrared filters and lenses

Formation and Properties of GeSe2–Ga2Se3–PbI2 Novel Chalcohalide Glasses

Thermal and optical properties of GeS2-based chalcogenide glasses

Spectroscopic properties of Er3+-doped chalco-halide glass ceramics

Glass Formation and Properties of Chalcogenides in A Gese2-As2se3-Pbse System

Thermal Properties, Microstructure, and Conductivity of New Glasses Based on the Gese2-Ga2se3-Agi System