Effect of the elemental substitution on threshold behaviours in Ge-As(Sb)-Se glasses
Xu Si-Wei,Wang Xun-Si,Shen Xiang,,
DOI: https://doi.org/10.7498/aps.73.20231797
IF: 0.906
2024-01-01
Acta Physica Sinica
Abstract:In this paper, We prepared two groups of the glasses, the first group is Ge x As 20 Se 80-x with x from 5 % to 32.5 %, the second group is Ge x Sb 20 Se 80-x with x from 5 % to 25 %, using the conventional melt-quench method, and investigated the effect of the elemental substitution of As by Sb on the threshold behaviors in Ge x As(Sb) 20 Se 80-x glasses. We aimed to understand that,to which degree the topological model and chemical order model can explain the correlation between the physical properties and glass compositions, and how the chemical composition can affect the transition threshold in the glasses. Glass transition temperature was measured by the differential scanning calorimeter (Mettler-Toledo, DSC1) with different scanning rates from 5 K/min to 30 K/min under a uniform nitrogen gas flow of 50 mL/min, the density of the glasses was measured by a Mettler H20 balance with a MgO crystal used as a reference. Samples from each glass composition were weighed five times and the average density was recorded, the refractive index of the glass at 1.5 um was measured by a Metricon Model 2010 prism coupler. Raman spectra were measured from a T64000 Jobin-Yvon-Horiba micro-Raman spectrometer equipped with a liquid-nitrogen-cooled CCD detector. The 830 nm laser line was used as an excitation source, and the laser power was kept as small as possible to avoid any photo-induced effects. The resolution of the spectrometer was about 0.5 cm -1 . The result from systematic measurements of these physical parameters shows that, while the transition thresholds at MCN=2.4 and 2.67 were verified in the Ge-As-Se glasses with ideal covalent network, these two transitions represent the covalent network structure inside the glass from an under-constrained “floppy” network to an over-constrained “rigid” phase and from the two-dimensional to the three-dimensional “stressed rigid” phase respectively. However, when As is substituted by Sb, the Ge x Sb 20 Se 80-x glass with non-ideal covalent network will change of the transition thresholds, which changes to the chemically stoichiometric composition. We further deconvolved Raman scattering spectra into different structural units and the change of their respective intensity showed the same behavior, and this was ascribed to the chemical effect induced by a large difference of the atomic radius between As and Sb, and a relatively strong ionic feature of the element Sb.
physics, multidisciplinary