Abstract:In this work, we report the sensitivity of structural, thermal, and electrical properties of Ag30+xAs28-xSe21Te21 (x = 2, 4, 6, 8, 10) chalcogenide glasses to the relative abundance of Ag and As in the compositions. The results show non-linear variation of glass density with linear increase in Ag (or decrease in As), implying structural change at 38 at.% Ag (or 20 at.% As). This structure change was further evident from differential scanning calorimetry (DSC) and Raman analyses, which show distinct characteristic temperatures (Tg, Tx, and Tp) and bonding type with increasing Ag content (decreasing As content). Specifically, at high Ag content beyond 38 at.% (As below 20 at.%), two additional exothermic peaks appear in DSC curves, and a strong As–Se bonding peak appears in Raman. The structural change is closely related to the variation of glass conductivity in a complex way, which first decreases with increasing Ag content, from 1.14 × 10−6 S cm−1 at 32 at.% Ag to 2.88 × 10−7 S cm−1 at 36 at.% Ag, but then with further increase in Ag, conductivity increases rapidly and reaches the maximum of 5.20 × 10−6 S cm−1 at the maximum Ag content 40 at.%. The abnormal change in conductivity is interpreted as due to the mutual effects of Ag doping as well as the degree of deviation from stoichiometry of the glass forming units. The impedance spectra identify little ionic contribution to the total conductivity which is supported from Raman spectra of the glasses and XRD analyses of the samples after thermal crystallization, both showing evidences of the presence of lone pair electrons of the chalcogen atoms. This work highlights the importance of compositional adjustment for the modification of physical properties in chalcogenide glasses, and provides a scientific basis for potential applications of such glasses in electronic devices.

Gamma ray irradiation induced optical band gap variations in chalcogenide glasses

Γ-Ray Irradiation Induced Multiple Effects on Ge–As–Se Chalcogenide Glasses

Gamma-ray-induced multi-effect on properties of chalcogenide glasses

Effect of Gamma Exposure on Chalcogenide Glass Films for Microphotonic Devices

Nanophase Separation and Effects on Properties of Ge–As–Se Chalcogenide Glasses

Spectroscopic properties of Er3+-doped chalco-halide glass ceramics

Properties of Chalcohalide Glasses in the Ge-As-Se-Te-I System

Glass forming region and optical properties of chalcogenide glasses within a gallium-tin-selenium ternary system

Understanding Aging in Chalcogenide Glass Thin Films Using Precision Resonant Cavity Refractometry

Effect of Gamma‐Ray Irradiation on the Optical Properties of PbO–B2O3–SiO2 and Bi2O3–B2O3–SiO2 Glasses

Properties of Dy3+‐Doped Ge–As–Ga–Se Chalcogenide Glasses

Optical Properties and Local Structure of Dy3+-doped Chalcogenide and Chalcohalide Glasses

Formation and Properties of Chalcogenide Glasses in the GeSe2-As2Se3-CdSe System

Optical properties and structural rigidity of [(GeSe2)75(Sb2Se3)25]100−xTex chalcogenide glasses for potential applications in infrared filters and lenses

Iodine-doped Ge-As-Se glasses with high purity and low dispersion

Mid-infrared femtosecond laser-induced damages in As2S3 and As2Se3 chalcogenide glasses

A Photo-Stable Chalcogenide Glass

Radiation-induced transmission spectral variations of Ce3+-doped heavy germanate glasses

Third-order optical nonlinearity in Ge-Se-Te chalcogenide glasses

Thermal and optical properties of GeS2-based chalcogenide glasses

Mutual effects of Ag doping and non-stoichiometric glass forming units on the structural, thermal, and electrical properties of Ag30+xAs28-xSe21Te21 chalcogenide glasses