Abstract:In this paper, We prepared two groups of the glasses, the first group is Ge x As 20 Se 80-x with x from 5 % to 32.5 %, the second group is Ge x Sb 20 Se 80-x with x from 5 % to 25 %, using the conventional melt-quench method, and investigated the effect of the elemental substitution of As by Sb on the threshold behaviors in Ge x As(Sb) 20 Se 80-x glasses. We aimed to understand that,to which degree the topological model and chemical order model can explain the correlation between the physical properties and glass compositions, and how the chemical composition can affect the transition threshold in the glasses. Glass transition temperature was measured by the differential scanning calorimeter (Mettler-Toledo, DSC1) with different scanning rates from 5 K/min to 30 K/min under a uniform nitrogen gas flow of 50 mL/min, the density of the glasses was measured by a Mettler H20 balance with a MgO crystal used as a reference. Samples from each glass composition were weighed five times and the average density was recorded, the refractive index of the glass at 1.5 um was measured by a Metricon Model 2010 prism coupler. Raman spectra were measured from a T64000 Jobin-Yvon-Horiba micro-Raman spectrometer equipped with a liquid-nitrogen-cooled CCD detector. The 830 nm laser line was used as an excitation source, and the laser power was kept as small as possible to avoid any photo-induced effects. The resolution of the spectrometer was about 0.5 cm -1 . The result from systematic measurements of these physical parameters shows that, while the transition thresholds at MCN=2.4 and 2.67 were verified in the Ge-As-Se glasses with ideal covalent network, these two transitions represent the covalent network structure inside the glass from an under-constrained “floppy” network to an over-constrained “rigid” phase and from the two-dimensional to the three-dimensional “stressed rigid” phase respectively. However, when As is substituted by Sb, the Ge x Sb 20 Se 80-x glass with non-ideal covalent network will change of the transition thresholds, which changes to the chemically stoichiometric composition. We further deconvolved Raman scattering spectra into different structural units and the change of their respective intensity showed the same behavior, and this was ascribed to the chemical effect induced by a large difference of the atomic radius between As and Sb, and a relatively strong ionic feature of the element Sb.

Study on devitrification and properties of GeAsS glass system

Nanophase Separation and Effects on Properties of Ge–As–Se Chalcogenide Glasses

Effect of some additives on crystallization and phase separation in glass systems Ge-Ga-S and Ge-As-S

STUDY OF PHASE-SEPARATION IN NA2O-B2O3-SIO2 GLASSES BY TEM AND OPTICAL DIFFRACTION

Intrinsic Nanoscale Phase Seperation of bulk As2S3 Glass

Thermal properties of chalcogenide glasses in the GeSe2–As2Se3–CdSe system

Effect of the elemental substitution on threshold behaviours in Ge-As(Sb)-Se glasses

FORMATION OF GeSe2-As2 Se3-CdSe INFRARED GLASSES

A Study of the Crystallization Kinetics of Ge-Te Amorphous Systems

Raman Scattering Studies of the GeS2–Ga2S3–CsCl Glassy System

Formation and Properties of Chalcogenide Glasses in the GeSe2-As2Se3-CdSe System

Structural transformation and rheological processes in bulk metallic glass Zr41Ti14Cu12.5Ni10Be22.5

Structural and vibrational characteristics of Ge-S-Br glass system: ab initio calculation and Raman study

Structural Study of Chalcogenide Glasses in the Bi5As35Se60-xTex System

Properties of Dy3+‐Doped Ge–As–Ga–Se Chalcogenide Glasses

Thermal and optical properties of GeS2-based chalcogenide glasses

Phase separation in mullite-composition glass

Intermediate phase, network demixing, boson and floppy modes, and compositional trends in glass transition temperatures of binary AsxS1-x system

Crystallization and chemical stability of GeS2-Ga2S3-CdS chalcogenide glasses

Crystallization Properties of Ge-Se-Bi Thermoelectric Glasses

Microstructure and thermal properties of the GeS 2 -In 2 S 3 -CsI glasses