Abstract:In this paper, a new process for the phase-separated P2O5-Al2O3 glass with SiO2-rich region is presented. The new method combines pneumatic atomization with mechanical stirring based on melting-quenching preparation. X-ray diffraction, Nano-infrared spectra, X-ray photoelectron spectra, Raman scattering spectra and atomic force microscope were carried out to investigate sample's structure and surface morphology. The results show that the phase-separated glasses consist of second phase, transition region and matrix region. The average diameter of separated phase, ie. 500 nm, 150 nm, 76 nm and 85 nm, depends on the diameter of SiO2 glass particles prepared by ball milling, that is 50 mu m, 10 mu m, 2 mu m and 400 nm respectively. Especially, transition region is formed by the connection of phosphorus oxygen tetrahedron and silicon oxygen tetrahedron, located between SiO2 region and matrix network region. After introducing the second phase, the Young's modulus of matrix glass was increased by 32.5% and the optimal value is 77.67 GPa within the scope of this experiment. It is attributed to that the formation of transition region increases the cross-linking of P2O5-Al2O3 glass network. The Young's modulus of the phase-separated glass increases with the diameter of the quartz glass particles decreases from 50 mu m to 2 mu m, but weakens at a diameter of 400 nm. The network polymerization due to increasing in the number of P3 units induced by second phase's diameter is responsible for rising in the Young's modulus, whereas too low diameter leads to particle agglomeration accompanied by the present of defects.

STUDY OF PHASE-SEPARATION IN NA2O-B2O3-SIO2 GLASSES BY TEM AND OPTICAL DIFFRACTION

Kinetics of Phase Separation of Soda-Lime-silica Glass with Minor P2O5 Additions

A Novel Method for Preparing Phase-Separated P2O5–Al2O3 Glass with High Young's Modulus

Phase Separation of Alkaline Earth Fluorosilicate Glass: A Strategy to Suppress Fluoride Evaporation

Structural evolution and phase separation of CaO • Al<sub>2</sub>O<sub>3</sub> • SiO<sub>2</sub> glasses in an electric field

Phase separation of CaO·Al2O3 ·SiO2 glasses induced by electric field

Phase-Separation and Crystallization in Fluorozirconate Glasses

Microstructure and Crystallization Behavior of Glasses in the ZrO2-ZnO-Al2O3-SiO2 System

In Situ Tem Study On Electron Irradiation Effects In Sio2-Na2o-B2o3 Glasses

Structural evolution and phase separation of CaO · Al 2 O 3 · SiO 2 glasses in an electric field

Phase Separation And Crystallization Of Li2o Center Dot Al2o3 Center Dot 4sio(2)-Ta2o5 Glass-Ceramics

Microstructure and crystallization behavior of glasses in the ZrO 2-ZnO-Al2O3-SiO2 system

The origin of phase separation in binary aluminosilicate glasses

Phase separation and crystallization of Li 2O · Al 2O 3 · 4SiO 2-Ta 2O 5 glass-ceramics

Ca<SUP>2+</SUP>/Sr<SUP>2+</SUP>/Ba<SUP>2+</SUP>dependent phase separation, nanocrystallization and photoluminescence in fluoroaluminosilicate glass

Raman Studies of the Phase Separation Mechanism of Cao-Al2o3-Sio2 Glasses in an Electric Field

Phase separation of CaO·B2O3·P2O5 glasses induced by polarization in an electric field

Effects of Mixed Alkaline Earth Oxides Additive on Crystallization and Structural Changes in Borosilicate Glasses

The effect of an electric field on the phase separation of Ag-doped glass

From Phase Separation to Nanocrystallization in Fluorosilicate Glasses: Structural Design of Highly Luminescent Glass-Ceramics

A study on the crystallization of CaO–Al2O3–SiO2 system glasses