Abstract:In recent years, phase separation glass has attracted extensive attention because of its unique structure and excellent properties. But its mechanism of phase separation on glass remains insufficient clear, especially, the influence of recombination time on structure and properties is unclear. Here, strengthened P2O5-Al2O3 glass with SiO2-Na2O high-silicate glass particles as the second phase was prepared by melting-quenching method combined with pneumatic atomization and mechanical stirring. The relationship between structure and mechanical properties of the glass was investigated by varying the recombination time. Experiment results showed that Young's modulus of the heterogeneous composite glass was higher than that of the P2O5-Al2O3 glass. Young's modulus of the sample firstly increased and then decreased with the recombination time increasing from 10 s to 8 min. The highest Young's modulus of 80.7 GPa was obtained at recombination time of 6 min, which was increased by 18% as compared with the P2O5- Al2O3 glass. Introducing SiO2-Na2O high-silicate glass particles not only formed the second phase in the matrix glass, but also changed the structure of the P2O5-Al2O3 glass. As the recombination time increases from 10 s to 6 min, coordination number of phosphorus in heterogeneous composite glass network gradually increases, while amount of non-bridging oxygen in the glass network gradually decreases, resulting in a gradual increase in network cross-linking. However, when the recombination time is more than 8 min, it is not conducive to network crosslinking. Therefore, development of heterogeneous composite glass can provide a new route for the preparation of glass materials with good damage resistance.

Kinetics of Phase Separation of Soda-Lime-silica Glass with Minor P2O5 Additions

A Novel Method for Preparing Phase-Separated P2O5–Al2O3 Glass with High Young's Modulus

STUDY OF PHASE-SEPARATION IN NA2O-B2O3-SIO2 GLASSES BY TEM AND OPTICAL DIFFRACTION

Effect of Recombination Time on the Structure and Properties of P2O5-Al2O3 Heterogeneous Composite Glass

Phase Separation And Crystallization Of Li2o Center Dot Al2o3 Center Dot 4sio(2)-Ta2o5 Glass-Ceramics

Phase separation and crystallization of Li 2O · Al 2O 3 · 4SiO 2-Ta 2O 5 glass-ceramics

The Role of Phosphate in the Glass Forming Region, Structure and Mechanical Properties for the SiO2-Al2O3-P2O5 System Contains High-Aluminum

Phase Separation of Alkaline Earth Fluorosilicate Glass: A Strategy to Suppress Fluoride Evaporation

Nucleation and crystallization kinetics of a multicomponent lithium disilicate glass by in situ and real-time synchrotron X-ray diffraction

Study on Phase Separation and Crystallization of Na2O-B2O3-SiO2-TiO2 Glass

Effect of P2O5/CaO on Crystallization and Phase Separation in Phosphatic Opal Glass

The origin of phase separation in binary aluminosilicate glasses

Two Types of Phase Separation and Crystal Nucleation-Growth Mechanisms for Machinable Glass Ceramic

EFFECT OF SPECIAL PHASE SEPARATION ON MICROSTRUCTURE AND PROPERTY OF GLASS-CERAMICS

From Phase Separation to Nanocrystallization in Fluorosilicate Glasses: Structural Design of Highly Luminescent Glass-Ceramics

Structural evolution and phase separation of CaO • Al<sub>2</sub>O<sub>3</sub> • SiO<sub>2</sub> glasses in an electric field

Phase separation of CaO·Al2O3 ·SiO2 glasses induced by electric field

Effect of P<SUB>2</SUB>O<SUB>5</SUB> on evolution of microstructure of MgO–Al<SUB>2</SUB>O<SUB>3</SUB>–SiO<SUB>2</SUB> glass ceramics

Phase separation of CaO·B2O3·P2O5 glasses induced by polarization in an electric field

Structural evolution and phase separation of CaO · Al 2 O 3 · SiO 2 glasses in an electric field

Phase separation in mullite-composition glass