Abstract:In this paper, We prepared two groups of the glasses, the first group is Ge x As 20 Se 80-x with x from 5 % to 32.5 %, the second group is Ge x Sb 20 Se 80-x with x from 5 % to 25 %, using the conventional melt-quench method, and investigated the effect of the elemental substitution of As by Sb on the threshold behaviors in Ge x As(Sb) 20 Se 80-x glasses. We aimed to understand that,to which degree the topological model and chemical order model can explain the correlation between the physical properties and glass compositions, and how the chemical composition can affect the transition threshold in the glasses. Glass transition temperature was measured by the differential scanning calorimeter (Mettler-Toledo, DSC1) with different scanning rates from 5 K/min to 30 K/min under a uniform nitrogen gas flow of 50 mL/min, the density of the glasses was measured by a Mettler H20 balance with a MgO crystal used as a reference. Samples from each glass composition were weighed five times and the average density was recorded, the refractive index of the glass at 1.5 um was measured by a Metricon Model 2010 prism coupler. Raman spectra were measured from a T64000 Jobin-Yvon-Horiba micro-Raman spectrometer equipped with a liquid-nitrogen-cooled CCD detector. The 830 nm laser line was used as an excitation source, and the laser power was kept as small as possible to avoid any photo-induced effects. The resolution of the spectrometer was about 0.5 cm -1 . The result from systematic measurements of these physical parameters shows that, while the transition thresholds at MCN=2.4 and 2.67 were verified in the Ge-As-Se glasses with ideal covalent network, these two transitions represent the covalent network structure inside the glass from an under-constrained “floppy” network to an over-constrained “rigid” phase and from the two-dimensional to the three-dimensional “stressed rigid” phase respectively. However, when As is substituted by Sb, the Ge x Sb 20 Se 80-x glass with non-ideal covalent network will change of the transition thresholds, which changes to the chemically stoichiometric composition. We further deconvolved Raman scattering spectra into different structural units and the change of their respective intensity showed the same behavior, and this was ascribed to the chemical effect induced by a large difference of the atomic radius between As and Sb, and a relatively strong ionic feature of the element Sb.

Composition dependence of the physical and acousto-optic properties of transparent Ge–As–S chalcogenide glasses

Correlation Between Acousto-Optic and Structural Properties of Ge–Sb–S Chalcogenide Glasses

Investigation of the Acousto‐optical Properties of Ge–As–Te–(Se) Chalcogenide Glasses at 10.6 Μm Wavelength

Thermal and optical properties of GeS2-based chalcogenide glasses

Investigation of the Ga-Sb-S Chalcogenide Glass with Low Thermo-Optic Coefficient As an Acousto-Optic Material

Chalcogenide Coatings of Ge_15Sb_20S_65 and Te_20As_30Se_50

Impact of structural changes of Ge–Sb–Se chalcogenide glasses on their acousto‐optic properties

Effect of the elemental substitution on threshold behaviours in Ge-As(Sb)-Se glasses

Novel acousto-optic material based on Ge-Te-AgI chalcohalide glasses

Properties of Dy3+‐Doped Ge–As–Ga–Se Chalcogenide Glasses

Mutual effects of Ag doping and non-stoichiometric glass forming units on the structural, thermal, and electrical properties of Ag30+xAs28-xSe21Te21 chalcogenide glasses

Intermediate phase, network demixing, boson and floppy modes, and compositional trends in glass transition temperatures of binary AsxS1-x system

Glass forming region and optical properties of chalcogenide glasses within a gallium-tin-selenium ternary system

Novel Ge-As-Se chalcogenide glass for potential high Brillouin gain coefficient of fiber

PROPERTIES OF GLASSES IN THE Ag2S–GeS2–As(Sb)2S3 SYSTEMS

Effects of the Se Substitution for Te on the Structure and Properties of Glasses in the Ag30As28(SexTe100-x)42 System

Properties of Chalcohalide Glasses in the Ge-As-Se-Te-I System

Improvement of the Faraday effect in Ge-S based chalcogenide glasses via gallium and lead compositional modifications

Thermal and Optical Properties of the Ga–Ge–Sb–Se Glasses

Iodine-doped Ge-As-Se glasses with high purity and low dispersion

Large and Ultrafast Third-Order Nonlinear Optical Properties of Ge-S Based Chalcogenide Glasses