Abstract:Nickel base superalloys are widely used in the preparation of hot end parts for aircraft engines because of their good comprehensive mechanical properties, oxidation resistance and structural stability. It's strengthened mainly by solid solution strengthening, gamma' phase strengthening and carbide strengthening. High alloying is one of the main methods to improve the solid solution strengthening level of nickel base superalloys, where the element W is an efficient alloying element with low price. The control of the W content is extremely important for high W content nickel base superalloys. However, there are few reports on the influence of W content on the microstructure of high W alloy. According to this background, by means of OM, SEM observation and XRD analysis, the influence of W content on the solidified microstructure in nickel base superalloy have been investigated in this work. Results show that when the W content is about 14% (mass fraction, the same below), there is no alpha-W phase being precipitated in the alloy. While as the content of W is higher than 16%, alpha-W could be precipitated during the solidification. On another hand, the grain size of the alloy decreases from 1.04 mm to 0.17 mm and the volume fraction of eutectic increases from 6% to 10% with the increase of the W content. While the content of W has no obvious effect on the sizes and morphologies of gamma' phase in the dendrite and inter-dendrite areas. During solidification, the a-W phase will be first precipitated due to its higher precipitation temperature, and the shrinkage of the residual liquid phase may cause the shift and growth of the alpha-W to the core of the liquid phase. The alpha-W could be as the core of the heterogeneous nucleation to reduce the critical nucleation energy, which is the main reason that the grain size of the 18%W alloy is smaller. During the growth of the dendrites with various orientations, the concentration of Al and Ti in the residual liquid phase may have a higher concentration gradient to cause the occurrence of eutectic transformation, which is the main reason that there is a higher volume fraction of eutectic in 18%W alloy.

Fabrication of Ultrafine-Grain and Great-Performance W–Ni–Fe Alloy with Medium W Content

Fabrication and Characterization of Tungsten Heavy Alloys with High W Content by Powder Metallurgy

A novel dissolution-precipitation mechanism during liquid phase sintering and its strengthening effects in W-Ni-Fe alloys with low W contents

Fine-grained 93W-4.9Ni-2.1Fe alloy with ultrahigh yield strength prepared via low temperature sintering of W nanocomposite powder

Fabrication, characterization, and mechanical properties of 93W–4.9Ni–2.1Fe/95W–2.8Ni–1.2Fe–1Al 2 O 3 heavy alloy composites

The Bifunctional Low Mismatch Nano Strengthening Phase Leads to a High Strength-Ductility W-Ta-Ni-Fe-Cu Alloy

Effect of Tungsten Content on Microstructure and Quasi-Static Tensile Fracture Characteristics of Rapidly Hot-Extruded W–Ni–Fe Alloys

Phase transformation and thermal stability of mechanically alloyed W–Ni–Fe composite materials

Fine-Grained Tungsten Heavy Alloy by Mechanical Alloying with Yttrium Oxide Addition

Fabrication of Fine-Grain Tungsten Heavy Alloy and Its Dynamic Failure Behavior

Fabrication and Properties of Novel NiWFeB Amorphous Alloys

Tungsten heavy alloy: Nano-crystallinity and alloying induced low temperature sintering, microstructure and mechanical properties

Microstructure and properties of liquid-phase sintered tungsten heavy alloys by using ultra-fine tungsten powders

Preparing Process of Fine-Grain Tungsten Heavy Alloy with High Mechanical Properties

Microstructure Evolution and Mechanical Properties of Ultra-Fine Grain AlCrFe2Ni2Wx High-Entropy Alloys

Microstructure and Properties of Ultra-Fine Tungsten Heavy Alloys Prepared by Mechanical Alloying and Electric Current Activated Sintering

Microstructure and Mechanical Properties of a Hot-Hydrostatically Extruded 93w–4.9ni–2.1fe Alloy

Fabricating Fine-Grained Tungsten Heavy Alloy by Spark Plasma Sintering of Low-Energy Ball-Milled W–2Mo–7Ni–3Fe Powders

Hot deformation behavior of a novel Ni–W–Co high-density Ni-based alloy with ultra-high W content

Influence of W Content on the Microstructure of Nickel Base Superalloy with High W Content

Fabrication of Ultra-Fine-Grained W-TiC Alloys by a Simple Ball-Milling and Hydrogen Reduction Method