Abstract:Ni–W–Co alloy is a recently developed single-phase Ni-based alloy with high density. An ultra-high content of W (35–38 wt%) is essential to ensure the high density but unfavorable to possess outstanding ductility or present large deformation. In this study, the flow stress behavior and hot workability of Ni–W–Co alloy were investigated through simulated compression tests with a temperature range of 1000–1300 °C and strain rate range of 0.01–5 s −1 . The Arrhenius-type constitutive equation at peak stress was established. The constitutive equation displays prediction bias due to the lower experimental values at low temperature and high strain rate. The ultra-high solution content of W not only results in the severely inhibited discontinuous dynamic recrystallization (DDRX) and high apparent deformation activation energy (568.5 kJ/mol) but also promotes the generation of subgrain boundaries. Furthermore, continuous dynamic recrystallization (CDRX) occurs during deformation at a low temperature and a high strain rate, which is quite different from the Ni-based alloy with a low W content that only DDRX occurs. The activation of CDRX shortens the stage at which work hardening dominates, and results in lower peak stress values. The prediction bias of the constitutive equation caused by the lower peak stress was eliminated through difference compensation. The hot processing maps at strain values of 0.3, 0.5, 0.7, and 0.9 were constructed. The optimal hot processing parameters of the Ni–W–Co alloy, which aims to obtain full recrystallization microstructure without defects, are strain rate 0.01–0.1 s −1 and temperature 1225–1300 °C in combination with the hot processing maps and microstructure evolution. This study provides a reference for the hot processing and microstructural modification of the novel Ni–W–Co alloy with an ultra-high W content.

Effect of Tungsten Content on Microstructure and Quasi-Static Tensile Fracture Characteristics of Rapidly Hot-Extruded W–Ni–Fe Alloys

Mechanical Properties and Thermal Shock Performance of W-Y2O3composite Prepared by High-Energy-rate Forging

Microstructure and Mechanical Properties of a Hot-Hydrostatically Extruded 93w–4.9ni–2.1fe Alloy

Effect Of Heat Treatment On Microstructure And Mechanical Properties Of Hot-Hydrostatically Extruded 93w-4.9ni-2.1fe Alloy

Tem Characterization of the Microstructure of Hot-Hydrostatically Extruded 93W-4.9Ni-2.1fe Alloy

Microstructure and mechanical properties of high density tungsten alloy and its influence factors

Influence of Hot Extrusion on Microstructure and Mechanical Properties of Tungsten Based Heavy Alloy

Revealing impact failure behavior of tungsten composite using instrumented Charpy impact testing

The W alloying effect on thermal stability and hardening of nanostructured Cu-W alloyed thin films

Effect of Heating Process on Fracture Behaviors of Wf/Cu82Al10Fe4Ni4 Composites

Fabrication of nanocrystalline supersaturated W–Al alloys with enhanced thermal stability and high sinterability

Effect of Tungsten Content on the Microstructure and Tensile Properties of Ni–xW–6Cr Alloys

Fabrication and Characterization of Tungsten Heavy Alloys with High W Content by Powder Metallurgy

Effects of Extrusion Deformation on Microstructure, Mechanical Properties and Hot Workability of Β Containing TiAl Alloy

Fine-grained 93W-4.9Ni-2.1Fe alloy with ultrahigh yield strength prepared via low temperature sintering of W nanocomposite powder

Hot deformation behavior of a novel Ni–W–Co high-density Ni-based alloy with ultra-high W content

The effect of fine W particles in matrix phase on mechanical properties of tungsten heavy alloys

Avoiding microstructural instabilities in high tungsten containing superalloys by adjusting Al content

Phase transformation and thermal stability of mechanically alloyed W–Ni–Fe composite materials

The simultaneous improvement of strength and ductility of the 93W-4.6Ni-2.4Fe prepared by additive manufacturing via optimizing sintering post-treatment

Microstructure Evolution and Recrystallization after Annealing of Tungsten Heavy Alloy Subjected to Severe Plastic Deformation