Abstract:The crystallization process of β zeolite has been investigated by using FT-IR, XRD, TG, SEM, and ICP-AES. The samples were obtained by hydrothermal synthesis at 140 °C and chemical composition of the mixture used for synthesis can be expressed as n(Al2O3) : n(SiO2) : n(TEABr) : n (Na2O) : n(NaF) : n(H2O) : n [(NH4)2O] = 1 : 25 : 7. 5 : 2. 5 : 3. 75 : 550 : 6. 25. The crystallization curve of zeolite β exhibits a typical S-shaped characteristic. The typical framework IR-absorptions at 567 and 518 cm-1 have different natures. The former is detected at the beginning of induction period and its intensity changes a little in induction period, but exhibits a direct correlation with crystallinity in growth period. The latter is not detected in the induction period, but exhibits the same trend in growth period. The large amorphous SiO2-Al2O3 particles which are visible at the beginning of crystallization change into small grains during the induction period. n(SiO2)/n(Al2O3) ratio of the solid phases obtained at different synthesis time changes significantly during the induction period, but changes a little in growth period. So the β zeolite crystal nucleus are formed via liquid-phase synthesis mechanism. A typical gel in synthesis of β zeolite is transformed initially into a solid, which contains richer aluminium, minor F- and occluded TEA species. The aluminosilicate gel particles are dissolved by F- during the induction period and the transition complex, which has a specific weak X-ray diffraction peak at 2θ = 22. 8° and specific DTG pattern, is formed at the turning point from induction period to growth period. During the growth period Si and Al transport from the liquid to the solid phase at almost the same rates. F- anion has greater influence on the formation and turning of transition complex.

Synthesis of STW-zeotype Germanosilicate via Steam-assisted Crystallization

Synthesis and Characterization of B-Substituted High-siliceous STW-type Silicate Zeolite

Synthesis of Pure-Silica Mtw Powder and Supported Films

Synthesis of hierarchically porous ZSM-5 zeolites by steam-assisted crystallization of dry gels silanized with short-chain organosilanes

Realizing the Direct Synthesis of High Silica IWS Zeolite with Improved Hydrothermal Stability

A Fluoride-Free Siliceous STW-type Zeolite Synthesized Using a Designed Organic Structure-Directing Agent

Crystallization Process of Zeolite ZSM-5 and Zeolite ZSM-35 in a Special Autoclave

Synthesis and Characterization of a Novel Microporous Framework Stannosilicate

Synthesis and Characterization of a Layered Silicogermanate PKU-22 and Its Topotactic Condensation to a Three-Dimensional STI-type Zeolite

Synthesis and characterization of WSiO_x mesoporous molecular sieve

Generalized High-Temperature Synthesis Of Zeolite Catalysts With Unpredictably High Space-Time Yields (Stys)

Synthesis and characterization of germanosilicate molecular sieves: GeO 2 /SiO 2 ratio, H 2 O/TO 2 ratio and temperature.

Preparation of ZSM-5 molecular sieve by diatomaceous earth in-situ crystallization

Mesoporogen-Free Synthesis of Hierarchically Structured Zeolites with Variable Si/Al Ratios via a Steam-Assisted Crystallization Process

Synthesis of β Zeolite Using Tetraethylammonium Bromide Together with Fluoride as Composite of Template (II) - Studies on Crystallization Process of β Zeolite

Transformation Behavior of Gibbsite to Boehmite by Steam-Assisted Synthesis

Different roles of CNTs in hierarchical HZSM-5 synthesis with hydrothermal and steam-assisted crystallization

Highly efficient synthesis of high-silica SSZ-13 zeolite by interzeolite transformation of L zeolite at higher temperature

Facile and fast synthesis of highly active Lewis acid MWW zeolite from a pure silica ITQ-1

Synthesis Of A Hierarchical Micro/Mesoporous Structure By Steam-Assisted Post-Crystallization

Direct Synthesis of Aluminosilicate IWR Zeolite from a Strong Interaction Between Zeolite Framework and Organic Template.