Abstract:Interzeolite transformation (IZT) is a powerful method for controlling the framework type, aluminum distribution, and hierarchical structures of zeolite. However, the in-depth mechanisms underlying IZT remain unexplored. In this study, we reveal a distinctive nucleation pathway and structural evolution of zeolite SSZ-13 during IZT that is different from the traditional hydrothermal synthesis methods. Utilizing two aluminum sources—al-rich zeolite analcite and aluminum sulfate—we accelerated the crystallization process with SSZ-13 seed crystals and TMAda-OH. Our findings indicate that the Al content, representing the charge density of the nucleation micro-environment, plays a critical role in shaping the framework and nucleation pathway. Nucleation occurred at the interface between analcite and the silica solution during IZT, characterized by a high-silica micro-environment with low charge density. In this environment, the precursor predominantly replicated the double six rings (D6R) of SSZ-13 seed fragments, forming double four rings (D4R) and CHA cages which resulted in a short induction period, fewer nucleation sites, and larger crystals size (∼1.5 μm). Conversely, when aluminum sulfate was mixed with silica sol, a uniform, Al-rich nucleation micro-environment with high negative charge density was established. the precursor primarily interacted with TMAda + ions for charge compensation rather than with seed fragments. This slow interaction promoted the formation of CHA cages instead of D6R and D4R, leading to a longer induction period, increased nucleation sites, and smaller SSZ-13 crystal sizes (∼150 nm). This study elucidates how the charge density of micro-environment mediated interaction between precursors, organic structure-directing agent, and seed, providing valuable insights into the crystallization kinetics of IZT.

Highly efficient synthesis of high-silica SSZ-13 zeolite by interzeolite transformation of L zeolite at higher temperature

Efficient synthesis of high-silica SSZ-13 zeolite and its catalytic performance in MTO reaction

Fast and efficient synthesis of SSZ-13 by interzeolite conversion of Zeolite Beta and Zeolite L

Synthesis Of Ssz-13 Zeolite With High Molar Ratio Of Sio2 To Al2o3 By Crystal Transformation Method Using Tetraethyl Ammonium Hydroxide As Template

Control of crystallization rate and morphology of zeolite silicalite-1 in solvent-free synthesis

Manipulation of the Crystallization of Ssz-13 Transformed from Coal Fly Ash-Derived Analcime

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Synthesis Of Zeolite Ssz-24 Using A Catalytic Amount Of Ssz-13 Seeds

Rapid and Efficient Synthesis of CHA-type Zeolite by Interzeolite Conversion of LTA-type Zeolite in the Presence of N, N, N-trimethyladamantammonium Hydroxide

Direct Synthesis of Aluminosilicate SSZ-39 Zeolite Using Colloidal Silica as a Starting Source

Sodium persulfate promoted interzeolite transformation of USY into SSZ-13 via a solid-state grinding route and its enhanced catalytic lifetime in the methanol-to-olefins reaction

Pickering emulsion mediated crystallization of hierarchical zeolite SSZ-13 with enhanced NH3 selective catalytic reduction performance

Direct Synthesis of SSZ-13 Zeolite Using Tetraethylammonium Hydroxide As an Efficient Organic Template in the Presence of Conventional Aluminum and Silicon Sources

Efficient and rapid transformation of high silica CHA zeolite from FAU zeolite in the absence of water

Generalized High-Temperature Synthesis Of Zeolite Catalysts With Unpredictably High Space-Time Yields (Stys)

Insight into the Growth Mechanism of Low-Temperature Synthesis of High-Purity Lithium Slag-Based Zeolite A

Synthesis of nanosheet SSZ-39 zeolite with enhanced catalytic performance in methanol-to-olefins reaction

Use of Borosilicate Seeds to Synthesize Aluminosilicate SSZ-82, a Zeolite Containing Intersecting 12- and 10-Membered Ring Channels

Enhanced Synthetic Efficiency of CHA Zeolite Crystallized at Higher Temperatures

Efficient Synthesis of All-silica DDR Zeolite

Charge density-mediated crystallization kinetics for SSZ-13 transformed from coal fly ash-derived Al-rich analcite