Abstract:Highly stable hierarchical ZSM-5 zeolites with intra-crystalline mesopores and inter-crystalline macropores have been synthesized via a steam-assisted conversion in the presence of polyethylene glycol. XRD, SEM, TEM, N-2 sorption and mercury intrusion measurement revealed that the irregular intra-crystal mesopores (2-10 nm) in each zeolite nanocrystal were generated by the removal of encapsulated PEG, and the inter-crystalline macropores (50-90 nm) were formed by the aggregation of the well crystallized ZSM-5 nanocrystals with a small size (50-200 nm). The ZSM-5 zeolite nanocrystals were achieved by a dense-gel with high TPA(+)/SiO2, highly concentrated TPA(+) can induce a burst in nucleation rate during the first step of steam-assisted conversion, which makes the dry gel easy to convert into zeolite nanocrystals, PEG arrested in the gel can be easily encapsulated by zeolite crystals during the steam-assisted conversion. Finally, these nanocrystals containing intra-crystalline mesopores aggregate into the bulky materials with an inter-crystalline macroporous network. In addition, the mesopore volume and external surface areas of Hier-ZSM-5 can be easily adjusted by changing the amount of PEG. Catalytic tests showed that Hier-ZSM-5 had a similar activity to Nano-ZSM-5, which must be collected by high-speed centrifugation; while had a higher activity than Con-ZSM-5, especially for the reactions involving large molecules. The high catalytic activity and easy separation from liquid mixture of Hier-ZSM-5 would facilitate its practical applications in chemical industry. Crown Copyright (c) 2013 Published by Elsevier B.V. All rights reserved.

Synthesis Of A Hierarchical Micro/Mesoporous Structure By Steam-Assisted Post-Crystallization

Facile Synthesis of Hierarchical Nanosized Single‐Crystal Aluminophosphate Molecular Sieves from Highly Homogeneous and Concentrated Precursors

Direct synthesis of hierarchical zeolites through mesoporous 3D wormhole framework using single-head quaternary ammonium salt as structure-directing agent

Mesoscale Reorganization of the Depolymerized Aluminosilicate into Single-Crystalline Hierarchical Zeolite

Enhanced Catalytic Oxidation by Hierarchically Structured TS-1 Zeolite

Mesoporogen-Free Synthesis of Hierarchically Structured Zeolites with Variable Si/Al Ratios via a Steam-Assisted Crystallization Process

Understanding Of The Dissolution-Crystallization Fabrication Strategy Towards Macro/Microporous Zsm-5 Single Crystals

Hierarchical Shell-Like ZSM-5 with Tunable Porosity Synthesized by Using a Dissolution-Recrystallization Approach.

One-Step Synthesis of Hierarchical ZSM-5 Using Cetyltrimethylammonium as Mesoporogen and Structure-Directing Agent

Highly Stable Hierarchical ZSM-5 Zeolite with Intra- and Inter-Crystalline Porous Structures

Synthesis of hierarchically porous ZSM-5 zeolites by steam-assisted crystallization of dry gels silanized with short-chain organosilanes

Synthesis and Characterisation of Hierarchically Structured Titanium Silicalite-1 Zeolites with Large Intracrystalline Macropores

Synthesis of ordered mesoporous alumina with large pore sizes and hierarchical structure

Controlling the primary particle evolution process towards silica monoliths with tunable hierarchical structure.

Synthesis of a hierarchical TS-1 zeolite with tunable macropore size and its performance in the catalytic oxidation reactions

Shape-controlled Synthesis of Monolithic ZSM-5 Zeolite with Hierarchical Structure and Mechanical Stability

Space-confined synthesis of nanorod oriented-assembled hierarchical MFI zeolite microspheres

Efficient Synthesis of Mesoporous Nano ZSM-5 Zeolite Crystals without a Mesoscale Template

Synthesis of Hierarchical MFI Zeolite Microspheres with Stacking Nanocrystals

Controllable synthesis of aluminosilica monoliths with hierarchical pore structure and their catalytic performance

Synthesis, characterization, and catalytic application of hierarchical nano-ZSM-5 zeolite