Highly Stable Hierarchical ZSM-5 Zeolite with Intra- and Inter-Crystalline Porous Structures

Haixiang Tao,Hong Yang,Xiaohui Liu,Jiawen Ren,Yanqin Wang,Guanzhong Lu

DOI: https://doi.org/10.1016/j.cej.2013.03.109

IF: 15.1

2013-01-01

Chemical Engineering Journal

Abstract:Highly stable hierarchical ZSM-5 zeolites with intra-crystalline mesopores and inter-crystalline macropores have been synthesized via a steam-assisted conversion in the presence of polyethylene glycol. XRD, SEM, TEM, N-2 sorption and mercury intrusion measurement revealed that the irregular intra-crystal mesopores (2-10 nm) in each zeolite nanocrystal were generated by the removal of encapsulated PEG, and the inter-crystalline macropores (50-90 nm) were formed by the aggregation of the well crystallized ZSM-5 nanocrystals with a small size (50-200 nm). The ZSM-5 zeolite nanocrystals were achieved by a dense-gel with high TPA(+)/SiO2, highly concentrated TPA(+) can induce a burst in nucleation rate during the first step of steam-assisted conversion, which makes the dry gel easy to convert into zeolite nanocrystals, PEG arrested in the gel can be easily encapsulated by zeolite crystals during the steam-assisted conversion. Finally, these nanocrystals containing intra-crystalline mesopores aggregate into the bulky materials with an inter-crystalline macroporous network. In addition, the mesopore volume and external surface areas of Hier-ZSM-5 can be easily adjusted by changing the amount of PEG. Catalytic tests showed that Hier-ZSM-5 had a similar activity to Nano-ZSM-5, which must be collected by high-speed centrifugation; while had a higher activity than Con-ZSM-5, especially for the reactions involving large molecules. The high catalytic activity and easy separation from liquid mixture of Hier-ZSM-5 would facilitate its practical applications in chemical industry. Crown Copyright (c) 2013 Published by Elsevier B.V. All rights reserved.