Abstract:The hierarchical zeolite ZSM-5 was synthesized in a CH3CH2OH-H2O hydrothermal system by using hexadecyltrimethyl ammonium bromide (CTAB) as sole template at a low crystallization temperature (130 degrees C). The effects of ethanol and CTAB on crystallization process and morphologies of ZSM-5 products were investigated. Ethanol molecules in synthesis system were beneficial to speed up crystallization, though crystal growth in NaOH-CTAB-H2O system was more difficult. The existence of CTAB resulted in highly crystalline and pure phase hierarchical ZSM-5 microspheres assembled by nanocrystals. The traces of crystallization evolution by XRD, FT-IR, N-2 adsorption/desorption, SEM/TEM, Si-29 MAS NMR, Al-27 MAS NMR spectra and TGA revealed that the hierarchical ZSM-5 microspheres were formed through the transformation of mesostructured amorphous aluminosilicates, in which the initial surfactant micelles were gradually excluded and thus acted as a molecule structure-directing agent to direct the crystallization of MFI nanozeolite. At the same time, the CTAB may disrupt nanocrystals further growth and aggregate them into hierarchical microsphere through CTA(+). Pyridine (Py) and pivalonitrile (Pn) adsorbed FT-IR spectra showed that the hierarchical ZSM-5 microspheres possessed large number of accessible acid sites due to the introduction of mesopores into zeolite. Therefore, it displayed much higher catalytic activities for both large molecules 1,3,5-trimethylbenzene (TMB) transformation and 1,3,5-triisopropylbenzene (TIPB) cracking reactions than conventional MFI zeolite, and the high selectivity to isomerization products (1,2,3- and 1,2,4-TMB) and benzene product from over-cracking.

Hierarchical Shell-Like ZSM-5 with Tunable Porosity Synthesized by Using a Dissolution-Recrystallization Approach.

Synthesis of ZSM-5 with Hierarchical Porosity: In-situ Conversion of the Mesoporous Silica-Alumina Species to Hierarchical Zeolite

Highly Stable Hierarchical ZSM-5 Zeolite with Intra- and Inter-Crystalline Porous Structures

Sub-micron sized hierarchical porous ZSM-5 particles with controllable mesoporous structures by changing the alkalinity in the synthesis using NaOH

Synthesis Of Hierarchical Zsm-5 Zeolites Via Two Stage Varying Temperature Crystallization With Enhanced Catalytic Cracking Performance

Hierarchically Tetramodal-Porous Zeolite ZSM-5 Monoliths with Template-Free-derived Intracrystalline Mesopores

Hierarchical ZSM-5 Zeolite Obtained by Designed Organosiloxane: Synthesis, Characterization, and Catalytic Applications

Shape-controlled Synthesis of Monolithic ZSM-5 Zeolite with Hierarchical Structure and Mechanical Stability

Facile synthesis of hierarchical porous ZSM-5 zeolite with tunable mesostructure and its application in catalytic cracking of LDPE

Postsynthesis of Hierarchical Core/shell ZSM-5 As an Efficient Catalyst in Ketalation and Acetalization Reactions

In-situ synthesis of hierarchical lamellar ZSM-5 zeolite with enhanced MTP catalytic performance by a facile seed-assisted method

A Hierarchical Zeolite Microsphere Prepared by an Eco-Friendly and Practical Route for Efficient Reaction of Bulky Molecules

Direct, Single-Step Synthesis of Hierarchical Zeolites Without Secondary Templating

Facile Synthesis of Mesostructured ZSM-5 Zeolite with Enhanced Mass Transport and Catalytic Performances

Facile Synthesis of Nano-Sized Hollow ZSM-5 Zeolites with Rich Mesopores in Shell

One-Step Synthesis of Hierarchical ZSM-5 Using Cetyltrimethylammonium as Mesoporogen and Structure-Directing Agent

Synthesis and Characterization of Hierarchical ZSM-5 Zeolites with Outstanding Mesoporosity and Excellent Catalytic Properties

Efficient Synthesis of Mesoporous Nano ZSM-5 Zeolite Crystals without a Mesoscale Template

Solid-state transformation of hollow silica microspheres into hierarchical ZSM-5 having tunable mesopores

Synthesis of hierarchical ZSM-5 zeolite in a rotating packed bed: Mechanism, property and application

Construction of monodispersed single-crystalline hierarchical ZSM-5 nanosheets via anisotropic etching