Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

Hierarchical Zsm-5 Catalyst Synthesized by A Triton X-100 Assisted Hydrothermal Method

EFFECT OF LONG CHAIN CATIONIC SURFACTANT ON ZSM-5 SYNTHESIS AND METHANOL TO OLEFIN REACTION

Synthesis and Physicochemical Characterization of Hierarchical ZSM-5: Effect of Organosilanes on the Catalyst Properties and Performance in the Catalytic Fast Pyrolysis of Biomass

A novel anionic surfactant as template for the development of hierarchical ZSM-5 zeolite and its catalytic performance

Hierarchical Shell-Like ZSM-5 with Tunable Porosity Synthesized by Using a Dissolution-Recrystallization Approach.

Enhanced Catalytic Oxidation by Hierarchically Structured TS-1 Zeolite

Shape-controlled Synthesis of Monolithic ZSM-5 Zeolite with Hierarchical Structure and Mechanical Stability

ZSM-5 Zeolite Single Crystals with B-Axis-aligned Mesoporous Channels As an Efficient Catalyst for Conversion of Bulky Organic Molecules.

Surfactant-assisted hydrothermal synthesis of core-shell ZSM-5@SSZ-13 zeolite for methanol to olefins reaction

One-Step Synthesis of Hierarchical ZSM-5 Using Cetyltrimethylammonium as Mesoporogen and Structure-Directing Agent

Rapid hydrothermal synthesis of hierarchical ZSM-5/beta composite zeolites

In-situ synthesis of hierarchical lamellar ZSM-5 zeolite with enhanced MTP catalytic performance by a facile seed-assisted method

Direct synthesis of H type ZSM-5 in shaped form and catalytic properties in methanol-to-hydrocarbon reaction

Caterpillar-shaped hierarchical ZSM-5 resulted from the self-assembly of regularly primary nano-sized zeolite crystals

Synthesis of Hierarchical Micro-mesoporous ZSM-5 Zeolite and its Catalytic Activity in Benzylation of Mesitylene

Facile synthesis of ultrafine nanosized ZSM-5 zeolite using a hydroxyl radical initiator for enhanced catalytic performance in the MTG reaction

Hierarchical ZSM-5 catalytic performance evaluated in the selective oxidation of styrene to benzaldehyde using TBHP

Hierarchically Tetramodal-Porous Zeolite ZSM-5 Monoliths with Template-Free-derived Intracrystalline Mesopores

Synthesis of Hierarchical ZSM‐11 Nanorods Aggregates and Catalytic Properties in Cyclohexene Hydration to Cyclohexanol

Si/Al Ratio Induced Structure Evolution During Desilication-Recrystallization of Silicalite-1 to Synthesize Nano-Zsm-5 Catalyst for MTH Reaction

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons