Synthesis and characterization of WSiO_x mesoporous molecular sieve

Tian Yan-wen

Abstract:This thesis emphasised on the synthesis of WSiOx with hexadecyl trimethyl ammonium chloride(CTAB) as template,tetraethyl orthosilicate(TEOS) as silica source,acetylacetone(HAcac)as assistant reagent,the modification of WSiOx was achieved by the route of one step in-situ to get the material loaded with transitional metal ammonium tungstate in neutral conditions.The characterization of WSiOx material was investigated by X-ray diffraction(XRD),N2 adsorption-desorption isotherms,FT-IR spectra,Scanning Electronic Microscope(SEM) analysis.The order degree of molecular mesoporous material was increased with the W content increasing to 6%;the calicination can not bring the pore to collapse;the pore performance was changed by the W addition,also,the W cannot destroy the molecular mesoporous sieve framework.The result showed that,the optimum W content is 5%,template is 1.8%,HAcac is 9%,the average pore diameter is 4.68 nm,the BET surface area is 966 m2/g.