Abstract:In this research, we report on the synthesis of mesoporous silicas with various quantities of immobilized oligosaccharide groups and different pore ordering degree. The hydrothermal co-condensation of tetraethyl orthosilicate and β-cyclodextrin-containing organosilane in the presence of cetyltrimethylammonium bromide template was employed. The purpose of this investigation was to show the opportunity of increasing β-cyclodextrin content in silica matrix by changing the molar ratio of initial reagents during organosilane synthesis and to determine whether the enhancing of immobilized groups on the surface influences on model aromatic compound adsorption from water. It was prepared several β-cyclodextrin-organosilanes by modification of (3-aminopropyl)triethoxysilane with oligosaccharide (the molar composition of reaction mixtures were 1:1, 3:1, and 5:1) with using N,N′-carbonyldiimidazole as linking agent. Three types of MCM-41 materials were obtained with 0.018, 0.072, and 0.095 mmol g−1 β-cyclodextrin-group loading according to chemical analysis of silicas. The IR spectroscopy and potentiometric titration were also performed to confirm the presence of functional groups in the silica matrix. Nitrogen sorptometry experiments exhibited the decrease of high surface area (from 812 to 457 m2 g−1) and the average pore diameter (from 1.06 to 0.60 cm3 g−1) of synthesized silicas with increasing of immobilized oligosaccharide groups. The influence of β-cyclodextrin-organosilane presence on the forming of hexagonally arranged porous structure of silicas was evaluated by X-ray diffraction and TEM analyses. As the loading of oligosaccharide groups increases in obtained silicas, the (100) reflex in diffraction patterns is even less intense and broader, denoting the decrease of long-range pore ordering. Adsorption experiments were carried out to study the effect of β-cyclodextrin groups’ attendance in silica matrix on benzene uptakes from aqueous solutions. Experimental kinetic curves of benzene adsorption on synthesized silicas were compared with theoretical models of Lagergren and Ho-McKay for pseudo-first and pseudo-second-order processes. Langmuir and Freundlich isotherm models were used to evaluate adsorption processes and parameters. Obtained β-cyclodextrin-containing MCM-41 silicas demonstrate adsorption level performance of known samples and could be very promising for benzene uptakes from aqueous solutions in water treatment processes.

Synthesis and Characterization of Functionalized Mesoporous Ethanesilica

Bifunctional Hybrid Mesoporous Organoaluminosilicates with Molecularly Ordered Ethylene Groups.

Continuous Synthesis of Mesoporous Y Zeolites from Normal Inorganic Aluminosilicates and Their High Adsorption Capacity for Dibenzothiophene (DBT) and 4,6-Dimethyldibenzothiophene (4,6-DMDBT)

Organic Groups Functionalised Mesoporous Silicates

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

Synthesis and Characterization of Stable Framework-Iron Containing Mesoporous Molecular Sieves Fe-Mcm-41

Mesoporous silica obtained with methyltriethoxysilane as co-precursor in alkaline medium

Functionalized silica materials synthesized via co-condensation and post-grafting methods

Structural Variety and Adsorptive Properties of Mesoporous Silicas with Immobilized Oligosaccharide Groups

Synthesis and Coating of Ordered Mesoporous Silica

Core-template-free Synthesis of Molecularly Ethane-Bridged Hollow Mesoporous Silica Spheres from Acid-Hydrolyzed Precursor

Synthesis and characterization of organic-inorganic hybrid mesoporous matierials with quaternary ammonium groups

Tailoring pore size of mesoporous silica and organosilica using biodegradable pentablock copolymer templates via EISA process

Synthesis and properties of aluminosilicate mesoporous material with adjustable pore structure

Phase Engineering of Hydrophobic Meso-Environments in Silica Particles for Technical Performance Enrichment

Synthesis and characterization of mesoporous and amorphous silica modified with silica-organo-sulfogroups

Benzene-Bridged Organosilica Modified Mesoporous Silica Nanoparticles via an Acid-Catalysis Approach

Synthesis of Ordered Cubic Periodic Mesoporous Organosilicas with Ultra-Large Pores

The Synthesis of Mesoporous Molecular Sieve MCM-48

Efficient Access to Functionalized Mesoporous Materials with Bicontinuous Morphologies via Kinetic Approach

Influence of synthesis parameters on the formation and structure of bimodal mesopore silica in a controlled sol-gel process