Abstract:Activated carbon (AC) was thermal treated under nitrogen and ammonia atmosphere, respectively, and used as a support to prepare Cu/AC catalyst by impregnation-calcination method. The influence of AC surface chemistry on the catalyst composition and Cu species particle size as well as the catalytic performace for oxidative carbonylation of methanol has been investigated. AC supports and their corresponding Cu/AC catalysts were characterized intensively by BET, XPS, XRD, H-2-TPR and TEM. The results indicate that the removal of most carboxylic groups by thermal treatment at 600 degrees C under nitrogen atmosphere can improve the Cu species dispersion and reduce the Cu species particle size. However, with further elevating the temperature to 800 degrees C, part of lactones, carboxylic anhydrides, phenol and ether groups were removed that lead to the Cu species agglomeration and sintering. Moreover, the decreased AC surface oxygen containing groups has weakened the precursor-support interaction and promoted the reduction of Cu2+ to Cu+ or Cu-0. Thermal treatment of AC under ammonia atmosphere results in that more surface oxygen containing groups were removed compared with nitrogen atmosphere. But nitrogen containing groups including pyridinic N (N-6), pyrrole nitrogen (pyrrolic-N) and quaternary nitrogen (N-Q) were introduced at the same time, which was conducive to the Cu species dispersion and reduction of particle size. Besides, the increased surface nitrogen containing groups has enhanced the precursor-support interaction and supressed the reduction of Cu2+ to Cu+ or Cu-0. The evaluation result reveals that the catalytic activity of the catalyst varies with the change of the particle size of Cu species. As Cu supported on AC thermal treated at 800 degrees C under ammonia atmosphere, the catalyst shows the optimum catalytic performance, which is ascribed to the smallest Cu species particle size (6-3 nm). The con. version of methanol, space-time yield and selectivity of dimethyl carbonate (DMC) are 9.6%, 278.7 mg.g(-1).h(-1) and 68.3%, respectively.

Effect of Activated Carbon Surface Chemistry on the Properties of Cu Particles and the Catalytic Performance for Oxidative Carbonylation of Methanol

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

Preparation of Chlorine-Free Cu/AC Catalyst and Its Catalytic Properties for Vapor Phase Oxidative Carbonylation of Methanol

Effect of Activated Carbon and Its Surface Property on the Activity of Ru/Ac Catalyst

Effect of Chemical Treatment of Activated Carbon As a Support for Promoted Dimethyl Carbonate Synthesis by Vapor Phase Oxidative Carbonylation of Methanol over Wacker-type Catalysts

Effect of Ultrasonic Treatment of Activated Carbon Support on Catalytic Performance of Ru/Ac for Ammonia Synthesis

Catalytic Performance of Cu_2(OH)_3Cl Catalysts Supported on Various Supports for Methanol Oxidative Carbonylation

Influences of preparation methods of ZrO2 support and treatment conditions of Cu/ZrO2 catalysts on synthesis of methanol via CO hydrogenation

Highly efficient super activated carbon supported ultra-low loading copper catalyst for the oxidative carbonylation of methanol to dimethyl carbonate

Effect of Ultrasonic Treatment on the Morphology of Activated Carbon and the Activities of Ba-Ru-K/Activated Carbon Catalyst

Silver catalysts supported over activated carbons for the selective oxidation of CO in excess hydrogen: effects of different treatments on the supports

Effect of Calcination Temperature on Catalytic Activity and Textual Property of Cu/HMOR Catalysts in Dimethyl Ether Carbonylation Reaction

The Role of Surface Properties of Activated Carbon in the Catalytic Reduction of NO by Carbon

Loading mechanism and double-site reaction mechanism of Cu on activated carbon for enhanced oxidation of CO from flue gas

Mechanistic Insight into Reaction Behaviors of Acetonitrile Catalytic Combustion over Cu-based Catalysts with Different Supports

Cu‐Fe/activated carbon catalyst for low‐temperature CO‐selective catalytic: Modification and denitration mechanism

Effect of N, P co-doped activated carbon supported Cu-based catalyst for acetylene hydration

Investigation of the interaction between Cu(acac)2 and NH4Y in the preparation of chlorine-free CuY catalysts for the oxidative carbonylation of methanol to a fuel additive

Surface Structure and Catalytic Performance of Cucl/Sio2-Al2o3 Catalysts for Methanol Oxidative Carbonylation

Effect of acid-treatment on the activated carbon of Ru/AC catalysts for catalytic decomposition of hydroxylamine nitrate and hydrazine nitrate