Effects of Preparation Condition and Support Modification on Ammonia Synthesis over Alumina-Supported Ruthenium Catalyst
XB Zhang,XN Li,C Huo,YQ Cen,YF Zhu,HZ Liu
DOI: https://doi.org/10.3321/j.issn:0253-9837.2002.03.005
IF: 16.5
2002-01-01
Chinese Journal of Catalysis
Abstract:The ruthenium catalyst supported on alumina was prepared by the method of incipient wetness impregnation. Ammonia synthesis over the catalyst was performed under the conditions; of 0 similar to 10 mpa, 425 or 475 degreesC, and space velocity of 20 000 h(-1) with synthesis gas of N-2-H-2, (1: 3). X-ray diffraction, nitrogen physical adsorption, and CO2 chemisorption were employed to characterize the phase, specific surface area, and surface basicity of alumina. With the increase of AI(OH)(3) calcination temperature from 600 to 900 degreesC, the surface basicity of alumina increased from 0.51 to 0.75 mmol/g, the specific surface area of alumina decreased from 223 to 140 m(2)/g. The calcination temperature of 800 degreesC gave the highest activity of Ba-Ru-K/Al2O3(39.38 mmol/(g(.) h) at 5 MPa and 475 degreesC). The presence of promoters K, Ba, and Sm increased significantly the activity of Ru/Al2O3, furthermore, promoters Ba, and Sm weakened the strong adsorption of hydrogen on the Ru sites, which increased greatly the activity of Ru/Al2O3 at high pressures. The surface basicity of alumina modified with MgO increased from 0.68 to 1.01 mmol/g, the specific surface area of alumina decreased from 168 to 72 m(2)/g, and the activity of Ba-Ru/Al2O3-MgO increased from 17.52 to 65.76 mmol/(g(.)h) (at 5 MPa and 475 V) when the mole content of MgO in alumina increased from 0 to 75 %. While the surface basicity, specific surface area of alumina modified with BaO, and the activity of Ru-K/Al2O3-BaO first increased and then decreased with the increase of the mole content of BaO in alumina from 0 to 33.3 %. When the mole content of BaO was equal to 7.7 %, the highest activity (34.47 mmol/g(.)h) at 5 MPa and 475 degreesC was obtained. If the mole content of BaO in alumina further increased, the specific surface area of alumina, and the activity of Ru-K/Al2O3-BaO would decrease dramatically because the Al2O3-BaO mixture oxide was present in the phase of BaAl2O3.