Mechanism of Hydrophobic Over-recovery on Polyethylene Surface Modified by Oxygen Plasma

Li Yupeng,Zhang Zhichao,Li Shengyao,Shi Wei,Lei Mingkai

DOI: https://doi.org/10.7503/cjcu20140253

2014-01-01

Abstract:Low density polyethylene (LDPE) surface was modified by oxygen capacitively coupled plasma (CCP) under a radio frequency(RF) power of 200 W for an exposure time of 1 min. The aging process of the plasma-modified LDPE was studied at aging temperatures of 60 and 90 degrees C for an aging time of 24 h. The morphology with the nanonodules was obtained on the as-modified LDPE surface under 200 W for 1 min and was stable on the post-aged LDPE surface at 60 and 90 degrees C after 24 h. The plasma modification under 200 W for 1 min introduced lots of polar oxygen-containing groups on the as-modified LDPE surface. The aging process at 60 degrees C after 24 h aroused the decrease of the polar oxygen-containing groups on the post-aged LDPE surface and lower oxygen-containing group content appeared on the post-aged surface at 90 degrees C. The as-modified hydrophilic surface with the contact angle of 42. 3 degrees underwent the hydrophobic recovery into hydrophobicity on the post-aged surface with the contact angle of 95. 9 degrees at 60 degrees C after 24 h similar to the original LDPE surface with 97. 2 degrees, and further hydrophobic over-recovery into higher hydrophobicity of the post-aged surface with the contact angle. of 104. 2 degrees at 90 degrees C after 24 h than the original surface. Based on the time-dependent contact angle model for the aging of the rough surface containing different wetting patches, the surface restructuring on the plasma-modified LDPE surface experiencing the hydrophobic over-recovery during aging process was quantitatively analysized.