A Study of Ultraviolet Irradiation Functionalization of LLDPE and Its Modification of PA66

Shi-Shan WU,Qian-Ping RAN,Yan-Ling LUO,Jian SHEN

DOI: https://doi.org/10.3321/j.issn:0251-0790.2005.10.049

2005-01-01

Abstract:The oxygen-contained groups such as C-O, C-OH, C = O, C(=O)O and C(=O)OH are introduced onto the molecular chains of linear low density polyethylene(LLDPE) through ultraviolet irradiation at environmental temperature of 70 degrees C in air without adding any additives. The concentration of these groups increases with the iucrease of irradiation time. The gel appears in irradiated LLDPE, the gel content increases with the iucrease of irradiation time. The melt flow index decreases and reach minimum when the irradiation time is 24 h, and then increase. The interfacial adhesion between irradiated LLDPE and polyamide 66 (PA66) and the mechanical properties of the PA66/irradiated LLDPE(80/20) blends are improved owing to the oxygen-contained polar groups introduced. Compared with those of PA66/LLDPE (80/20) blends, the tensile strength, Young's modulus, bending strength and notch impact strength of PA66/irradiated LLDPE(80/20) blends for 24 It are increased from 48.3, 908, 64.8 Wa and 31 J/m [PA66/LLDPE (80/20) blend] to 62.0, 984, 83.1 Wa and 85 J/m, respectively.