STUDIES ON FUNCTIONALIZATION OF HIGH DENSITY POLYETHYLENE AND ITS COMPATIBILIZATION EFFECT

吴石山,徐僖

DOI: https://doi.org/10.3321/j.issn:1000-3851.2002.04.004

2002-01-01

Abstract:The effect of the ultraviolet irradiation at different environmental temperatures in air on the structure and properties of high density polyethylene (HDPE) and the compatibilization effect of HDPE functionalized by the ultraviolet irradiation on HDPE/polyvinyl alcohol (PVA)-fiber blend systems are studied through FTIR, surface contact angle measurement with water and mechanical properties test. The results show that -C(C=O)CH3, -CH2C(=O)CH2-, -C(=O)O-oxygen-containing groups are introduced onto the HDPE molecular chain during the ultraviolet irradiation in air. The rate of HDPE functionalization is increased with the rise of the environmental temperature. After the ultraviolet irradiation, the Young's modulus and the tensile yield strength of HDPE are increased; its elongation at break and the notched Izod impact strength are decreased. The proper functionalized HDPE behaves as a compatibilizer in the HDPE/PVA-fiber blend; by adding 5 wt% functionalized HDPE (the irradiation light intensity is 78 W/m2 and the irradiation time is 24 hours) into the HDPE/PVA-fiber (88/12 wt%), the tensile yield strength and the notched Izod impact strength of the blend are increased from 28.3 MPa (HDPE/PVA-fiber: 88/12 wt%) to 30.6 MPa and 130 J/m to 163 J/m respectively.