Abstract:The structure and properties of high density polyethylene (HDPE) functionalized by ultraviolet irradiation at different light intensities in air were studied by electron analysis, FTIR spectroscopy, contact angle with water, differential scanning calorimetry and mechanical properties measurement. The results show that oxygen-containing groups such as C=O, C-O and C(=O)O were introduced onto the molecular chain of HDPE following irradiation, and the rate and efficiency of HDPE functionalization increased with enhancement of irradiation intensity. After irradiation, the melting temperature, contact angle with water and notched impact strength of HDPE decreased, the degree of crystallinity increased, and their variation amplitude increased with irradiation intensity. Compared with HDPE, the yield strength of HDPE irradiated at lower light intensity (32 W m(-2) and 45 W m(-2)) increases monotonically with irradiation time, and the yield strength of HDPE irradiated at higher light intensity (78 W m(-2)) increases up to 4S h and then decreased with further increase in irradiation time. The irradiated HDPE behaved as a compatibilizer in HDPE/polycarbonate (PC) blends, and the interface bonding between HDPE and PC was ameliorated. After adding 20 wt% HDPE irradiated at 78 W m(-2) irradiation intensity for 24 h to HDPE/PC blends, the tensile yield strength and notched Izod impact strength of the blend were increased from 26.3 MPa and 51 J m(-1) to 30.2 MPa and 158 J m(-1), respectively. (C) 2003 Society of Chemical Industry.

Studies on Fast Functionalization of HDPE by Ultraviolet Irradiation and Functionalized HDPE/CaCO3 Composites

Study on the Surface Energy of HDPE Functionalizied Through Ultraviolet Light Irradiation

Studies on Quick Functionalization of Polyethylene Through Ultraviolet Irradiation and Its Composites

Study on Structure and Properties of HDPE Functionalized by Ultraviolet Irradiation in Air and O2 Atmosphere

Studies On High Density Polyethylene (Hdpe) Functionalized By Ultraviolet Irradiation And Its Application

A STUDY ON ULTRAVIOLET IRRADIATION FUNCTIONALIZATION OF HDPE

STUDIES ON FUNCTIONALIZATION OF HIGH DENSITY POLYETHYLENE AND ITS COMPATIBILIZATION EFFECT

Studies on Hdpe Functionalized by Ultraviolet Irradiation and Interfacial Interaction of Hdpe/Stc Blend

Studies on Structure and Properties of Hdpe Functionalized Through Ultraviolet Irradiation and Its Blends with Caco3

Effect of the Reaction Atmosphere on High-Density Polyethylene Functionalized by Ultraviolet Irradiation

Compatibilization of irradiated HDPE

Effect of Reaction Temperature on Hdpe Functionalized Through Ultraviolet Irradiation

Effects of different treatments on the interface and mechanical properties of high density polyethylene reinforced by sericite-tridymite-cristobalite

Structure and properties of irradiated HDPE high-density polyethylene/calcium carbonate composites

Effect of ultraviolet light irradiation intensity on chemical structure and compatibilization of HDPE to HDPE/PC blend

A study on ultraviolet irradiation modification of high-density polyethylene and its effect in the compatibility of HDPE/PVA fibre composites

Fast Functionalisation of Polypropylene (pp) by Ultraviolet Irradiation and Compatibilised Pp/Caco3 Composite

Studies of Modification of Hdpe and Interfacial Interaction of Its Composites with Sericite

Impact of Ultraviolet Radiation on HDPE and HDPE/STC Blends

Thermal and thermo-oxidative degradation of high density polyethylene/fullerene composites

The Effects of Irradiation Cross-Linking on the Thermal Degradation and Flame-Retardant Properties of the Hdpe/Eva/Magnesium Hydroxide Composites