Abstract:Carbon nanotubes (CNT) were grown on a carbon fiber surface via a chemical vapor deposition method, and a CNT reinforced Cf/SiC composite was fabricated via a polymer impregnation and pyrolysis process. In this work, we studied the mechanical properties of microscale areas, such as fiber-matrix interfaces modified by CNT, CNT reinforced matrices, and fiber-CNT-matrices in CNT reinforced Cf/SiC hybrid composites. A combination of Vickers indentation and nanoindentation techniques was adopted to elucidate the relationship between the microscopic and macroscopic mechanical properties of the composites. Nanoindentation was used to test the interfacial bonding strength between the fiber and matrix and the hardness of matrices with embedded CNTs. Vickers indentation was used to study the failure behavior of fiber-CNT-matrix units. Interfacial bonding strength was found to be obviously improved by the presence of in situ grown CNTs. Interfacial debonding occurred at the fiber/pyrolytic carbon interphase but not the pyrolytic carbon/CNT interface, indicating that the interface where CNTs were grown possessed a higher bonding strength. Unfortunately, the nanohardness and modulus of the CNT reinforced matrix (Hv=7.5±1.2 GPa, E=62±5.0 GPa) was lower than that of the matrix without CNT (Hv=11.4±0.3 GPa, E=88.0±1.8 GPa). High resolution transmission electron microscope (TEM) images of the CNT/matrix interface showed that the graphitic structure of the CNT wall was likely damaged. This damage of the CNTs and the resulting reduced matrix properties were thought to be caused by serious chemical reaction between CNTs and the Si-C-O amorphous matrix. Vickers indentation measurements were used to determine the combined properties of fiber-CNT-matrix unit. Because whole Vickers indentations were not as clear as those for the pure ceramic, the exact Vickers hardness was not obtained. The indentation size was used to evaluate the damage resistance of the fiber-CNT-matrix unit. Surprisingly, the indentations in the composite with CNTs were smaller than those in composite without CNTs, indicating that the damage resistance of the whole fiber bundle was improved by CNT addition. Thus, the improved fiber/matrix interfacial bonding strength offset the negative effect of the decreased matrix properties. In addition, the damaged CNT-reinforced matrix remained integrated, while the matrix without CNTs showed a crushed morphology. The cracks were bridged by CNTs, and pull-out of CNTs in the cracks were considered responsible for the improved damage tolerance. The increases in debonding toughness and pull-out toughness caused by the CNTs were theoretically calculated. The simulation indicated that the toughening effect of the CNTs may be further improved if the CNT/matrix interface is suitably tailored and the CNTs are well protected.

Enhanced thermal and mechanical properties of optimized SiC<sub><i>f</i></sub>/SiC composites with in-situ CNTs on PyC interface

Enhanced Thermal and Mechanical Properties of Optimized SiCf/SiC

Enhanced thermal and mechanical properties of optimized S i C f / S i C composites with in-situ CNTs on PyC interface

Properties of Carbon Nano-Tubes–cf/sic Composite by Precursor Infiltration and Pyrolysis Process

The Improvement in the Mechanical and Thermal Properties of SiC/SiC Composites by Introducing CNTs into the PyC Interface

The Improvement of Mechanical Properties of SiC/SiC Composites by in Situ Introducing Vertically Aligned Carbon Nanotubes on the PyC Interface

Enhanced Thermal Conductivity and Mechanical Properties of 2D C F/sic Composites Modified by In-Situ Grown Carbon Nanotubes

Enhancing the Tensile Properties of SiC Composites by a Two-Dimensional CNT Film

In-situ Grown Carbon Nanotubes and Their Applications for SiCf/SiC Composites

Mechanical Properties of SiCf/SiC Composites Reinforced by In-Situ Grown Carbon Nanotubes

Enhancing Thermal Conductivity of C/SiC Composites Containing Heat Transfer Channels

Effects of SiO2-coated CNTs on the Directional Formation of SiC Whiskers and Improvement in the Ablative Resistance of Polymer-Matrix Composites

Depositing CNTs on the Interface and Surface of C/PyC/SiCs for Tunable Mechanical and Electromagnetic Properties

Thermal and Mechanical Properties of Sic/Sic-Cnts Composites Fabricated by Cvi Combined with Electrophoretic Deposition

The Mechanical Properties of Microscale Area in CNT-C&lt;sub&gt;f&lt;/sub&gt;/SiC Hierarchical Composite

Mechanical Properties and Oxidation Resistance of Phenolic Formaldehyde Interlocking CNTs-C-f/SiC Composite

Carbon Nanotubes Introduced in Different Phases of C/PyC/SiC Composites: Effect on Microstructure and Properties of the Materials

In-situ synthesis and microstructural evolution of a SiC reinforced Al-50Si composite exhibiting exceptional thermal properties

Mechanical properties and strengthening mechanism of SiCf/SiC mini-composites modified by SiC nanowires

Study on C/C composites modified by in-situ vapor-grown carbon nanofibers

The mechanical properties and thermal conductivity of carbon/carbon composites with the fiber/matrix interface modified by silicon carbide nanofibers