Abstract:A water-based route has been demonstrated for synthesizing ZnSe and Cd-doped ZnSe (ZnSe(ZnxCd1-xSe, 0 < x < 1) quantum dots (QDs) that have tunable and narrow photo luminescence (PL) peaks from the ultraviolet A (UVA) to the blue range (350-490 nm) with full-width at half-maximum (fwhm) values of 24-36 nm. Hydrazine (N2H4) was used to maintain oxygen-free conditions, allowing the reaction vessel to be open to air. The properties of the QDs were controlled using the thiol ligands, 3-mercaptopropionic acid (MPA), thiolglycolic acid (TGA), and L-glutathione (GSH). On the basis of optical spectra, linear three-carbon MPA attenuated nucleation and growth, yielding small ZnSe QDs with a high density of surface defects. In contrast, TGA and GSH produced larger ZnSe QDs with lower surface defect densities. The absorption spectra show that growth was more uniform and better controlled with linear two-carbon TGA than branched bifunctional GSH. After 20 min of growth TGA-capped ZnSe had an average diameter of 2.5 nm based on high-resolution transmission electron microscopy images; these nanocrystals had an absorbance peak maximum of approximately 340 nm (3.65 eV) and a band gap PL emission peak at 372 nm (3.34 eV). Highly fluorescent ZnxCd1-xSe QDs were fabricated by adding a Cd-thiol complex directly to ZnSe QD solutions; PL peaks were tuned in the blue range (400-490 nm) by changing the Zn to Cd ratio. The Cd-bearing nanocrystals contained proportionally more Se based on X-ray photoelectron spectroscopy, and Cd-Se bonds had ionic character, in contrast to primarily covalent Zn-Se bonds.

One-Pot Synthesis of CdSe Quantum Dots Using Selenium Dioxide As a Selenium Source in Aqueous Solution

A Redox Reaction to Synthesize Nanocrystalline Cu2-xSe in Aqueous Solution

Synthesis and Characterization of Monodisperse CdSe Quantum Dots with Zinc Blende Structure

Synthesis of Highly Luminescent Mercaptosuccinic Acid-Coated Cdse Nanocrystals under Atmospheric Conditions

Aqueous synthesis of CdSe and CdSe/CdS quantum dots with controllable introduction of Se and S sources

Synthesis of Highly Emissive CdSe Quantum Dots by Aqueous Precipitation Method

A Facile Route for Highly Efficient Color-Tunable Cu-Ga-Se/ZnSe Quantum Dots

Simple Synthesis of Highly Luminescent Water-Soluble CdTe Quantum Dots with Controllable Surface Functionality

One-Pot Synthesis of Biocompatible CdSe/CdS Quantum Dots and Their Applications as Fluorescent Biological Labels

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

An Improved One-Pot Aqueous Phase Synthesis Of Cdte Qds

Rapid Aqueous Synthesis of High-quality CdTe Colloidal Quantum Dots

Aqueous synthesis of highly monodispersed thiol-capped CdTe quantum dots through electrochemical approach.

Aqueous Synthesis of Highly Luminescent CdTe Quantum Dots and Its Growth Mechanism

Rapid synthesis of NADPH responsive CdSe quantum dots from selenium nanoparticles

Aqueous Synthesis and Fluorescence-Imaging Application of Cdte/Znse Core/Shell Quantum Dots with High Stability and Low Cytotoxicity

Controlled Synthesis and Characterization of Znse Quantum Dots

One-Pot Large-Scale Synthesis of Robust Ultrafine Silica-Hybridized CdTe Quantum Dots

Synthesis of Green CdSe/chitosan Quantum Dots Using a Polymer-Assisted Γ-Radiation Route

Synthesis and characterization of ZnSe and ZnSe/ZnS quantum dots for potential biomedical application

Large Stokes Shift of Ag Doped CdSe Quantum Dots Via Aqueous Route