Abstract:In this work, we developed a simple method for synthesizing CdSe/ZnSe/ZnS multishell quantum dots (QDs). CdSe/ZnSe core/shell QDs was synthesizd using one step injection of zinc precursor into the crude solution of the CdSe reaction system and then CdSe/ZnSe/ZnS core/shell/shell QDs were obtained by epitaxially growing a ZnS shell on the CdSe/ZnSe surface. Introducing a middle shell (ZnSe) sandwiched between CdSe core and ZnS outer shell allows considerably reduce strain inside nanocrystals because ZnSe have the lattice parameter intermediate to those of CdSe and ZnS. In comparison with the method reported previously, our synthesis method effectively simplifies the experimental operation, shortens the experimental period and reduces the waste of the chemcals. The annealing process was used to improve the fluorescence quantum yield of the QDs after the shell growth. The resulting CdSe/ZnSe/ZnS multishell QDs was further characterized in detail. Transmission electron microscopy indicated that the QDs are spherical and the shell is successfully coated on the surface of the CdSe QDs. The size of CdSe core is 2.8 nm, and the size of the CdSe cores with CdSe/ZnSe and CdSe/ZnSe/ZnS shells are determined to be 4 and 5 nm, respectively. The X-ray powder diffraction patterns suggested that the core (CdSe) and shell (ZnSe and ZnS) of the CdSe/ZnSe/ZnS QDs have a pure cubic phase. The luminescence properties of the QDs were investigated by means of photoluminescence and ultraviolet-visible absorption spectra. The results indicated the CdSe/ZnSe/ZnS QDs exhibit a high photoluminescence quantum yield. Besides, it can be seen that the absorption and photoluminescence bands shift to the red during the shell growth due to the large extension of the electronic wave function into the shell material. For the potential biological application, the CdSe/ZnSe/ZnS QDs were transferred into water phase from an organic phase by surface ligand exchange with mercaptopropionic acid. The water-soluble QDs with a quantum yield of about 17% have compatible functional chemical groups.

Aqueous synthesis of CdSe and CdSe/CdS quantum dots with controllable introduction of Se and S sources

Synthesis of high-quality CdSe quantum dots in aqueous solution

Synthesis and Characterization of the CdSe/ZnSe/ZnS Multishell Quantum Dots

Synthesis of CdSe Quantum Dots (qds) in the Water

Aqueous Synthesis of Luminescent CdSe Quantum Dots from Selenium Tetrachloride

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

Photo-assisted synthesis of highly fluorescent ZnSe(S) quantum dots in aqueous solution

Synthesis of Highly Emissive CdSe Quantum Dots by Aqueous Precipitation Method

Water-Soluble Cdse and Cdse/Cds Nanocrystals: A Greener Synthetic Route

Aqueous synthesis of Cu-doped ZnSe quantum dots

Water-Soluble Fluorescent CdTe/ZnSe Core/Shell Quantum Dot: Aqueous Phase Synthesis and Cytotoxicity Assays

Aqueous Synthesis of Highly Luminescent CdSe Quantum Dots with Narrow Spectra Using Hydrazine Hydrate Reduction Selenium

Aqueous Synthesis of CdTe/CdS/ZnS Quantum Dots and Their Optical and Chemical Properties

Facile and Green Synthesis of Core–shell ZnSe/ZnS Quantum Dots in Aqueous Solution

A Facile Colloid Aqueous Method for Synthesis of Water Soluble ZnSe Quantum Dots with High Fluorescence and Stability Characterization

A simple and novel route for the synthesis of water soluble ZnSe quantum dots using the Nano-Se as the reaction intermediate

A simple organic synthesis for CdS and Se-doped CdS nanocrystals

An innovative chalcogenide transfer agent for improved aqueous quantum dot synthesis

Simple Synthesis of Highly Luminescent Water-Soluble CdTe Quantum Dots with Controllable Surface Functionality

Highly Photoluminescent Water-Soluble ZnSe/ZnS/ZnS Quantum Dots Via Successive Shell Growth Approach

One-Pot Synthesis of CdSe Quantum Dots Using Selenium Dioxide As a Selenium Source in Aqueous Solution