Abstract:Successive ion layer adsorption and reaction (SILAR) originally developed for the deposition of thin films on solid substrates from solution baths is introduced as a technique for the growth of high-quality core/shell nanocrystals of compound semiconductors. The growth of the shell was designed to grow one monolayer at a time by alternating injections of air-stable and inexpensive cationic and anionic precursors into the reaction mixture with core nanocrystals. The principles of SILAR were demonstrated by the CdSe/CdS core/shell model system using its shell-thickness-dependent optical spectra as the probes with CdO and elemental S as the precursors. For this reaction system, a relatively high temperature, about 220-240 degrees C, was found to be essential for SILAR to fully occur. The synthesis can be readily performed on a multigram scale. The size distribution of the core/shell nanocrystals was maintained even after five monolayers of CdS shell (equivalent to about 10 times volume increase for a 3.5 nm CdSe nanocrystal) were grown onto the core nanocrystals. The epitaxial growth of the core/shell structures was verified by optical spectroscopy, TEM, XRD, and XPS. The photoluminescence quantum yield (PL QY) of the as-prepared CdSe/CdS core/shell nanocrystals ranged from 20% to 40%, and the PL full-width at half-maximum (fwhm) was maintained between 23 and 26 nm, even for those nanocrystals for which the UV-vis and PL peaks red-shifted by about 50 nm from that of the core nanocrystals. Several types of brightening phenomena were observed, some of which can further boost the PL QY of the core/shell nanocrystals. The CdSe/CdS core/shell nanocrystals were found to be superior in comparison to the highly luminescent CdSe plain core nanocrystals. The SILAR technique reported here can also be used for the growth of complex colloidal semiconductor nanostructures, such as quantum shells and colloidal quantum wells.

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

Synthesis of CdSe and CdTe Nanocrystals Without Precursor Injection.

Single Step Synthesis of CdSeS Nanorods with Chemical Composition Gradients

A simple organic synthesis for CdS and Se-doped CdS nanocrystals

Synthesis of Highly Luminescent Mercaptosuccinic Acid-Coated Cdse Nanocrystals under Atmospheric Conditions

Facile Phosphine-Free Synthesis of CdSe/ZnS Core/Shell Nanocrystals Without Precursor Injection

Noninjection Facile Synthesis of Gram-Scale Highly Luminescent Cdse Multipod Nanocrystals

Synthesis of photoluminescent colloidal CdS nanocrystals via a non-injection method

Preparation and Tunable Photoluminescence of Alloyed CdS X Se 1− X Nanorods

Synthesis and optical properties of CdS nanorods and CdSe nanocrystals using oleylamine as both solvent and stabilizer

Synthesis of CdS nanocrystals by a new method

Synthesis Of Cdse, Znse, And Znxcd1-Xse Nanocrystals And Their Silica Sheathed Core/Shell Structures

Alternative Routes Toward High Quality CdSe Nanocrystals

Noninjection ultralarge-scaled synthesis of shape-tunable CdS nanocrystals as photocatalysts

Large scale synthesis of stable tricolor Zn(1-x)Cd(x)Se core/multishell nanocrystals via a facile phosphine-free colloidal method.

Controlled Synthesis of High Quality Type-Ii/Type-I Cds/Znse/Zns Core/Shell1/Shell2 Nanocrystals

Synthesis of Monodisperse Nanocrystals Via Microreaction: Open-to-Air Synthesis with Oleylamine As a Coligand.

Large-scale Synthesis of Nearly Monodisperse CdSe/CdS Core/shell Nanocrystals Using Air-Stable Reagents Via Successive Ion Layer Adsorption and Reaction.

Facile and Green Route to Highly Luminescent ZnS-shelled CdSe Nanocrystals

A Method to Synthesize CdSe Nanocrystals

Synthesis of Monodisperse CdSe Nanocrystals:Nucleation and Growth