Abstract:Here we report a new "green" method to synthesize Zn(1-x)Cd(x)Se (x = 0-1) and stable red-green-blue tricolor Zn(1-x)Cd(x)Se core/shell nanocrystals using only low cost, phosphine-free and environmentally friendly reagents. The first excitonic absorption peak and photoluminescence (PL) position of the Zn(1-x)Cd(x)Se nanocrystals (the value of x is in the range 0.005-0.2) can be fixed to any position in the range 456-540 nm. There is no red or blue shift in the entire reaction process. Three similar sizes of alloyed Zn(1-x)Cd(x)Se nanocrystals with blue, green, and yellow emissions were successfully selected as cores to synthesize high quality blue, green, and red core/shell nanocrystal emitters. For the synthesis of core/shell nanocrystals with a high quantum yield (QY) and stability, the selection of shell materials has been proven to be very important. Therefore, alternative protocols have been used to optimize thick shell growth. ZnSe/ZnSe(x)S(1-x) and CdS/Zn(1-x)Cd(x)S have been found as an excellent middle multishell to overcoat between the alloyed Zn(1-x)Cd(x)Se core and ZnS outshell. The QYs of the as-synthesized core/shell alloyed Zn(1-x)Cd(x)Se nanocrystals can reach 40-75%. The Cd content is reduced to less than 0.1% for Zn(1 -x)Cd(x)Se core/shell nanocrystals with emissions in the range 456-540 nm. More than 15 g of high quality Zn(1-x)Cd(x)Se core/shell nanocrystals were prepared successfully in a large scale, one-pot reaction. Importantly, the emissions of such thick multishell nanocrystals are not susceptible to ligand loss and stability in various physiological conditions.

Preparation and Tunable Photoluminescence of Alloyed CdS X Se 1− X Nanorods

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

Single Step Synthesis of CdSeS Nanorods with Chemical Composition Gradients

Single crystalline CdS nanorods fabricated by a novel hydrothermal method

Synthesis of Single Crystalline CdS Nanorods by a PVP-assisted Solvothermal Method

Preparation and tunable mid-IR optical properties of ternary Cd_{1-x}Pb_xS nanocrystals by mechanical alloying

Good Optical Properties of Branched CdS Nanoparticles and Its Large Area Growth via Solvothermal Route

Synthesis of Highly Luminescent Mercaptosuccinic Acid-Coated Cdse Nanocrystals under Atmospheric Conditions

Controllable synthesis, characterization and photoluminescence properties of morphology-tunable CdS nanomaterials generated in thermal evaporation processes

Band-gap engineering of semiconductor nanowires through composition modulation.

Spatial bandgap engineering along single alloy nanowires.

Controlled synthesis and luminescence of semiconductor nanorods.

Synthesis of high aspect ratio quantum-size CdS nanorods and their surface-dependent photoluminescence

Characteristics and Optical Properties of Cd1−xMnxS Nanorods Prepared Through Hydrothermal Route

A review on the synthesis methods of CdSeS-based nanostructures

Selective Synthesis and Characterization of CdSe Nanorods and Fractal Nanocrystals

Large scale synthesis of stable tricolor Zn(1-x)Cd(x)Se core/multishell nanocrystals via a facile phosphine-free colloidal method.

Room-Temperature Broad-Wavelength-Tunable Single-Mode Lasing from Alloyed CdS 1- x Se x Nanotripods

Composition-tunable vertically aligned CdS(x)Se(1-x) nanowire arrays via van der Waals epitaxy: investigation of optical properties and photocatalytic behavior.

Preparation and Spectral Properties of Pvp-Modified Cds Nanorods

Surface Modification and Enhancement of Luminescence Due to Quantum Effects in Coated Cdse/Cuse Semiconductor Nanocrystals