Abstract:A water-based route has been demonstrated for synthesizing ZnSe and Cd-doped ZnSe (ZnSe(ZnxCd1-xSe, 0 < x < 1) quantum dots (QDs) that have tunable and narrow photo luminescence (PL) peaks from the ultraviolet A (UVA) to the blue range (350-490 nm) with full-width at half-maximum (fwhm) values of 24-36 nm. Hydrazine (N2H4) was used to maintain oxygen-free conditions, allowing the reaction vessel to be open to air. The properties of the QDs were controlled using the thiol ligands, 3-mercaptopropionic acid (MPA), thiolglycolic acid (TGA), and L-glutathione (GSH). On the basis of optical spectra, linear three-carbon MPA attenuated nucleation and growth, yielding small ZnSe QDs with a high density of surface defects. In contrast, TGA and GSH produced larger ZnSe QDs with lower surface defect densities. The absorption spectra show that growth was more uniform and better controlled with linear two-carbon TGA than branched bifunctional GSH. After 20 min of growth TGA-capped ZnSe had an average diameter of 2.5 nm based on high-resolution transmission electron microscopy images; these nanocrystals had an absorbance peak maximum of approximately 340 nm (3.65 eV) and a band gap PL emission peak at 372 nm (3.34 eV). Highly fluorescent ZnxCd1-xSe QDs were fabricated by adding a Cd-thiol complex directly to ZnSe QD solutions; PL peaks were tuned in the blue range (400-490 nm) by changing the Zn to Cd ratio. The Cd-bearing nanocrystals contained proportionally more Se based on X-ray photoelectron spectroscopy, and Cd-Se bonds had ionic character, in contrast to primarily covalent Zn-Se bonds.

Synthesis of Green CdSe/chitosan Quantum Dots Using a Polymer-Assisted Γ-Radiation Route

Green Synthesis of Highly Efficient CdSe Quantum Dots for Quantum-Dots-sensitized Solar Cells

Synthesis and Characterization of Monodisperse CdSe Quantum Dots with Zinc Blende Structure

Synthesis of Highly Emissive CdSe Quantum Dots by Aqueous Precipitation Method

Synthesis And Characterization Of Water-Soluble Cdse/Cds/Zns Core-Shell Quantum Dots

A Facile Synthesis of Biocompatible, Glycol Chitosan Shelled CdSeS/ZnS QDs for Live Cell Imaging.

Aqueous synthesis of CdSe and CdSe/CdS quantum dots with controllable introduction of Se and S sources

Preparation of CdSe Quantum Dots with Full Color Emission Based on a Room Temperature Injection Technique.

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

Green Synthesis of CdS/CISe Core‐Shell Structured Quantum Dots and Their Photovoltaic Applications

A Facile Route for Highly Efficient Color-Tunable Cu-Ga-Se/ZnSe Quantum Dots

Water-Soluble Cdse and Cdse/Cds Nanocrystals: A Greener Synthetic Route

One-step fabrication of biocompatible chitosan-coated ZnS and ZnS:Mn 2+ quantum dots via a γ-radiation route

Fabrication of the CdSeTe Alloyed and CdSeTe/ZnS Core-Shell Quantum Dots

Preparation and characterization of CdS quantum dots chitosan biocomposite

Large Stokes Shift of Ag Doped CdSe Quantum Dots Via Aqueous Route

Fabrication of near-infrared-emitting CdSeTe/ZnS core/shell quantum dots and their electrogenerated chemiluminescence.

Photo-assisted synthesis of highly fluorescent ZnSe(S) quantum dots in aqueous solution

Synthesis and Characterization of High Fluorescence, Type-Ⅱ Core/Shell CdTe/CdSe Quantum Dots in Aqueous Medium

Aqueous synthesis of highly monodispersed thiol-capped CdTe quantum dots through electrochemical approach.

A new and straightforward synthesis route for preparing Cds quantum Dots