Abstract:Non-stoichiometric copper selenide (Cu2-x Se, x = 0.18 similar to 0.25) nanomaterials have attracted extensive attentions due to their excellent thermoelectric, optoelectronic and photocatalytic performances. However, efficient production of Cu2-x Se nanoparticles (NPs) through a green and convenient way is still hindered by the inevitable non-environmentally friendly operations in common chemical synthesis. Herein, we initially reveal the coexistence of seleninic acid content and elemental selenium (Se) NPs in pulsed laser-generated Se colloidal solution. Consequently, we put forward firstly a closed-cycle reaction mode for totally green production of Cu1.8Se NPs to exclude traditional requirements of high temperature and toxic precursors by using Se colloidal solution. In such closed-cycle reaction, seleninic acid works as the initiator to oxidize copper sheet to release cuprous ions which can catalyze the disproportion of Se NPs to form SeO2-x Se NPs, and the by-product SeO32- ions promote subsequent formation of cuprous from the excessive Cu sheet. In experiments, the adequate copper (Cu) sheet was simply dipped into such Se colloidal solution at 70 degrees C, and then the stream of Cu1.8Se NPs could be produced until the exhaustion of selenium source. The conversion rate of Se element reaches to more than 75% when the size of Se NPs in weakly acidic colloidal solution is limited between 1 nm and 50 nm. The laser irradiation duration shows negative correlation with the size of Se NPs and unobvious impact to the pH of the solution which both are essential to the high yield of Cu1.8Se NPs. Before Cu sheet is exhausted, Se colloidal solution can be successively added without influences to the product quality and the Se conversion rate. Such green methodology positively showcases a brand-new and potential strategy for mass production of Cu2-xSe nanomaterials.

A Redox Reaction to Synthesize Nanocrystalline Cu2-xSe in Aqueous Solution

Synthesis of nanocrystalline lead chalcogenides PbE (E = S, Se, or Te) from alkaline aqueous solutions

A Hydrothermal Method for Low-Temperature Growth of Nanocrystalline Pyrite Nickel Diselenide

Synthesis of Cu2–xSe Nanocrystals by Tuning the Reactivity of Se

Synthesis of nanocrystalline Cu(2-x)Se at room temperature by γ-irradiation

Room Temperature Synthesis of Cubic Nanocrystalline CdSe in Aqueous Solution

A Simple, Convenient, Mild Hydrothermal Route to Nanocrystalline CuSe and Ag2Se

Colloidal synthesis of monodisperse quaternary CuInSSe nanocrystals

Alkylthiol-enabled Se Powder Dissolution in Oleylamine at Room Temperature for the Phosphine-Free Synthesis of Copper-Based Quaternary Selenide Nanocrystals.

An Aqueous Approach to ZnSe and CdSe Semiconductor Nanocrystals

Cu2−xSe nanooctahedra: controllable synthesis and optoelectronic properties

Synthesis of Nanocrystalline Cu2 Xse at Room Temperature by Γ-Irradiation

Room Temperature Redox Reaction to Prepare AgCuSe Ternary Nanorods

Facile synthesis of CuSe nanoparticles and high-quality single-crystal two-dimensional hexagonal nanoplatelets with tunable near-infrared optical absorption

Formation of Cu2−xSe(en)2 in a Solvothermal Process and Conversion to Nanocrystalline Cu2−xSe

Sonochemical Synthesis of Copper Selenides Nanocrystals with Different Phases

A Novel Solid–liquid Route for the Preparation of Cu3Se2 and Ag2Se Nanocrystals

Novel Closed-Cycle Reaction Mode for Totally Green Production of Cu 1.8 Se Nanoparticles Based on Laser-Generated Se Colloidal Solution

Size-, Shape-, and Assembly-Controlled Synthesis of Cu2−xSe Nanocrystalsvia a Non-Injection Phosphine-Free Colloidal Method

Facile Synthesis of Ag-doped ZnCdS Nanocrystals and Transformation into Ag-doped ZnCdSSe Nanocrystals with Se Treatment

Chemical Synthesis of Nanostructured Cu2se with High Thermoelectric Performance