Abstract:AgCuSe nanorods were prepared at room temperature by a redox reaction. The as-prepared product was characterized by X-ray powder diffraction, transmission electron microscopy and X-ray photoelectron spectroscopy.X-ray powder diffraction shows that the as-prepared product is the tetragonal phase of AgCuSe. Transmission electron microscopy shows that the sample consists of nanorods with a diameter varying from 5 nm to 20 nm and a length varying from 200 nm to 600 nm. X-ray photoelectron spectroscopy shows that the purity of the sample is high. The formation mechanism of AgCuSe and the growth mechanism of AgCuSe nanorods were discussed.Thermodynamic calulations show that the final product in the synthetic system is pure AgCuSe. The solvent ethylenediamine did not only acts a didentate ligand to form relatively state Ag + and Cu + complexes, but also dissolved Se and enhanced the reactivity of Se. It played an important role in controlling the nucleation and growth of AgCuSe nanorods.

Room Temperature Redox Reaction to Prepare AgCuSe Ternary Nanorods

A Redox Reaction to Synthesize Nanocrystalline Cu2-xSe in Aqueous Solution

A Novel Room Temperature Method to Nanocrystalline Ag2se

Single Step Synthesis of CdSeS Nanorods with Chemical Composition Gradients

A Dry Method To Synthesize Dendritic Ag2se Nanostructures Utilizing Cdse Quantum Dots And Ag Thin Films

A Simple, Convenient, Mild Hydrothermal Route to Nanocrystalline CuSe and Ag2Se

Synthesis and characterization of Sb2Se3 nanorods

Synthesis of nanocrystalline Cu(2-x)Se at room temperature by γ-irradiation

One-Step Hydrothermal Preparation of ZnSe Nanorods and Their Characterization

Elemental Solvothermal Reaction to Produce Ternary Semiconductor CuInE2 (E = S, Se) Nanorods.

Synthesis of Nanocrystalline Cu2 Xse at Room Temperature by Γ-Irradiation

Preparation of Ag2Se and Ag2Se1−xTex Nanowires by Electrodeposition from DMSO Baths

Chemical Synthesis, Structural Characterization, Optical Properties, and Photocatalytic Activity of Ultrathin ZnSe Nanorods.

Preparation of CdSe Quantum Dots with Full Color Emission Based on a Room Temperature Injection Technique.

Room Temperature Growth of Rod-Like Nanocrystalline Ag2Te in Mixed Solvent

Synthesis of Cdse nanocrystals in aqueous solution

Synthesis and Characterization of Ternary CuInS2 Nanorods Via a Hydrothermal Route

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

Preparation of Monodisperse Se Colloid Spheres and Se Nanowires Using Na 2 SeSO 3 As Precursor

Unraveling the Formation of Ternary AgCuSe Crystalline Nanophases and Their Potential as Antibacterial Agents

Selective Synthesis and Characterization of CdSe Nanorods and Fractal Nanocrystals