Abstract:A clean, facile route of using only common bulk selenium (Se) powder and silver (Ag) foil in a simple solvothermal process is developed to synthesize a film of silver selenide (Ag2Se) dendrites of highly oriented (001) nanocrystals. The simple process takes similar to 10 h at 160 degrees C in a common alcohol such as methanol or ethanol in an autoclave, and the reaction time is shorter than in many prevalent methods. The adoption of elemental Se and Ag (foil) in the synthesis eases the control of the purity of the product, simplifies the reaction steps, and reduces the costs, as the synthesis does not require Se and Ag compounds, and also requires no chemical additives other than an alcohol as solvent. The results support a mechanism of dissolution of the bulk-like Se powder in the solvothermal process, transport of solvated Se to react with Ag, nucleation of Ag2Se nanocrystals, surface-mediated, solvation-assisted surface diffusion of Ag2Se nanocrystals, and diffusion-limited aggregation of the Ag2Se nanocrystals through oriented attachment for the growth of dendrites having highly oriented (001) nanocrystals. The clean, relative facile route is practical for the fabrication of Ag2Se crystals/films with hierarchically ordered nanostructures for future applications in solar cell devices. More importantly, the same concept can be adopted for the synthesis of other nanomaterials with bulk elemental reactants with no reliance on chemical compounds or additives.

A Simple, Convenient, Mild Hydrothermal Route to Nanocrystalline CuSe and Ag2Se

A Redox Reaction to Synthesize Nanocrystalline Cu2-xSe in Aqueous Solution

A Hydrothermal Method for Low-Temperature Growth of Nanocrystalline Pyrite Nickel Diselenide

A Novel Solid–liquid Route for the Preparation of Cu3Se2 and Ag2Se Nanocrystals

An Aqueous Approach to ZnSe and CdSe Semiconductor Nanocrystals

Preparation and Characterization of Nanocrystalline Cu2−xSe by a Novel Solvothermal Pathway

Formation of Cu2−xSe(en)2 in a Solvothermal Process and Conversion to Nanocrystalline Cu2−xSe

A Novel One-Step Solvothermal Route to Nanocrystalline CuSbS2 and Ag3SbS3

Hydrothermal synthesis and characterization of CuIn2.0Se3.5 nanocrystallites

The synthesis and characterization of nanocrystalline Cu- and Ag-based multinary sulfide semiconductors

A Dry Method To Synthesize Dendritic Ag2se Nanostructures Utilizing Cdse Quantum Dots And Ag Thin Films

A Novel Room Temperature Method to Nanocrystalline Ag2se

Sonochemical Synthesis of Silver, Copper and Lead Selenides

Room-Temperature Synthesis of Copper and Silver, Nanocrystalline Chalcogenides in Mixed Solvents

Hydrothermal Preparation of Sb2Se3 Nanocrystals

Alkylthiol-enabled Se Powder Dissolution in Oleylamine at Room Temperature for the Phosphine-Free Synthesis of Copper-Based Quaternary Selenide Nanocrystals.

Syringe pump-assisted synthesis of water-soluble cubic structure Ag2Se nanocrystals by a cation-exchange reaction.

Simple, convenient, mild solvothermal route to nanocrystalline Cu3P and Ni2P

A convenient, low temperature route to nanocrystalline SnSe

Solvothermal Synthesis to Cu2snse4 Nanocrystals at Low Temperature

Using Elemental Se and Ag to Grow Pure Ag2Se Dendrites/Dendritic-Films of Highly Oriented (001) Nanocrystals