Abstract:Transition metal diselenides (MSe2, M=Ni, Co, Fe) were synthesized successfully through a simple solvothermal-reduction reaction at low temperatures. EDXA and XPS techniques confirmed that the compositions of these diselenides were in good agreement with their stoichiometries. With increasing temperature, the obtained NiSe2 transformed from initial filament nanocrystallites to final octahedral crystals. The studies on the thermal stability of the as-prepared NiSe2 showed that NiSe acted in an intermediate role in the pyrolysis process. The Raman spectrum of NiSe2 presented the peak of the Se-Se stretching mode at 216.5 cm(-1). XRPD techniques revealed that the as-prepared CoSe2 at higher temperature had an orthorhombic structure similar to that of FeSe2. At low temperature this orthorhombic phase CoSe2, which displayed rodlike shape with the growth direction along < 121 >, coexisted with a trace of the cubic phase CoSe2.

A Simple Synthetic Method for MSe2 (m=fe, Co or Ni) Nanocrystallites at Low Temperature

A Hydrothermal Method for Low-Temperature Growth of Nanocrystalline Pyrite Nickel Diselenide

A Redox Reaction to Synthesize Nanocrystalline Cu2-xSe in Aqueous Solution

The synthesis of CuFeSe2 through a solventothermal process

A Simple, Convenient, Mild Hydrothermal Route to Nanocrystalline CuSe and Ag2Se

A Simple Method for the Preparation of Nanocrystalline Transition Metal Sulfides

Preparation and Characterization of Nanocrystalline Cu2−xSe by a Novel Solvothermal Pathway

A direct solvothermal route to nanocrystalline selenides at low temperature

A Novel Room Temperature Method to Nanocrystalline Ag2se

Selenium Nanotubes Synthesized by A Novel Solution Phase Approach

Wet Synthesis and Characterization of Mse (M = Cd, Hg) Nanocrystallites at Room Temperature

Shape Control and Characterization of Transition Metal Diselenides Mse2 (M = Ni, Co, Fe) Prepared by A Solvothermal-Reduction Process

The synthesis and morphological control of nanocrystalline pyrite nickel disulfide and cobalt disulfide

A Solvothermal Route to Nanocrystalline Cu7Te4 at Low Temperature

Low-Temperature Hydrothermal Synthesis of Transition Metal Dichalcogenides

Synthesis and Characterization of Nanocrystalline Bi2Se3 by Solvothermal Method

A Low Temperature Route to Nanocrystalline Co9S8

Synthesis of Nanocrystalline Cobalt Selenide in Nonaqueous Solvent

Solvothermal Synthesis of Nanocrystalline MoS2from MoO3and Elemental Sulfur

Formation of Cu2−xSe(en)2 in a Solvothermal Process and Conversion to Nanocrystalline Cu2−xSe

Solvothermal Route to Nanocrystalline CdSe