Abstract:The CoS nanocrystals were synthesized by a solvethermal method,using Co(NO3)2-6H2O and thiourea as raw materials.Composition,particle size and surface morphology of the samples were characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM) and transmission electron microscopy(TEM).The results show that the as-prepared material are CoS nanoparticles at 180 ℃,witch diameter is about 40 nm.Powder production rate increases with increasing temperature,when the reaction temperature rises to 180 ℃,the yield close to 60%.When temperature further increases to 200 ℃,the yield remains unchanged,but abnormal grain growth happened.Addition of dispersant PEG can effectively control the size of the particles and inhibit the reunite of products.In additions,higher degree of crystallinity of the CoS nanocrystals can be synthesized by reducing the content of organic solvent EG,but it is not beneficial to control powder particle size,because the reaction rate is too fast.

A Low Temperature Route to Nanocrystalline Co9S8

A Hydrothermal Method for Low-Temperature Growth of Nanocrystalline Pyrite Nickel Diselenide

Hydrazine-controlled hydrothermal synthesis of Co 9 S 8 from a homogeneous solution

Hydrazine-controlled hydrothermal synthesis of Co<sub>9</sub>S<sub>8</sub> from a homogeneous solution

Preparation and characterization of Co 9 S 8 nanocrystalline and nanorods

A New Chemical Route to Prepare Nanocrystalline Cobalt Monoarsenide

Studies on the nanocrystalline Co3O4 by wet synthesis and its microstructure

Synthesis and characterization of nanocrystalline NiSb and NiSb2 at low temperature

The synthesis and morphological control of nanocrystalline pyrite nickel disulfide and cobalt disulfide

Hydrothermal-controlled Synthesis of Hexagonal Co9S8 Single Crystal Flake

Single crystalline CdS nanorods fabricated by a novel hydrothermal method

Preparation and Phase Transformation of Nanocrystalline Copper Sulfides (cu9s8, Cu7S4 and CuS) at Low Temperature

Solvothermal synthesis and characterization of cobalt sulfide nanocrystals

Controlled Synthesis of Cobalt Sulfide Nanocrystalline by Ultrasonic Spray Pyrolysis Process

Nanocrystalline Pyrite Cobalt Disulfide Synthesized by Solvent-thermal Preparation

Organo-thermal Preparation of Nanocrystalline Cobalt Phosphides

Preparation of nanocrystalline nickel powders through hydrothermal-reduction method

A Hydrothermal Reduction Route to Single‐Crystalline Hexagonal Cobalt Nanowires

Moderate temperature synthesis of nanocrystalline Co3O4 via gel hydrothermal oxidation

Solvent–thermal Preparation of Nanocrystalline Pyrite Cobalt Disulfide

Preparation and characterization of nanocrystalline nickel monosulfide(h) via the ethanol-thermal reducing process