Abstract:The low evaporation temperature and carcinogen classification of commonly used molybdenum trioxide (MoO3) precursor render it unsuitable for the safe and practical synthesis of molybdenum disulfide (MoS2). Furthermore, as evidenced by several experimental findings, the associated reaction constitutes a multistep process prone to the formation of uncontrolled amounts of intermediate MoS2-yOy phase mixed with the MoS2 crystals. Here, molybdenum dioxide (MoO2), a chemically more stable and safer oxide than MoO3, was utilized to successfully grow cm-scale continuous films of monolayer MoS2. A high-resolution optical image stitching approach and Raman line mapping were used to confirm the composition and homogeneity of the material grown across the substrate. A detailed examination of the surface morphology of the continuous film revealed that, as the gas flow rate increased by an order of magnitude, the grain-boundary separation dramatically reduced, implying a transition from a kinetically to thermodynamically controlled growth. Importantly, the single-step vapor-phase sulfurization (VPS) reaction of MoO2 was shown to suppress intermediate state formations for a wide range of experimental parameters investigated and is completely absent, provided that the global S:Mo loading ratio is set higher than the stoichiometric ratio of 3:1 required by the VPS reaction.

Solvothermal Synthesis of Nanocrystalline MoS2from MoO3and Elemental Sulfur

Preparation of Single-Layer MoS(2x)Se2(1-x) and Mo(x)W(1-x)S2 Nanosheets with High-Concentration Metallic 1T Phase.

Hydrothermal synthesis and characterization of laminar MoS2

Synthesis and characterization of porous nanoparticles of molybdenum sulfide (MoS2) chalcogenide semiconductor prepared by polymerizing-complexing sol–gel method

Solvothermal synthesis of ternary Cu2 MoS4 nanosheets: structural characterization at the atomic level.

Phase transitions and controlled sulfurization of molybdenum oxides in vacuum

Tube- and ball-like amorphous MoS2 prepared by a solvothermal method

Controlling Dispersion and Morphology of MoS2 Nanospheres by Hydrothermal Method Using SiO2 As Template

Application of Hydrothermal and Solvothermal Method in Synthesis of MoS2

The synthesis and morphological control of nanocrystalline pyrite nickel disulfide and cobalt disulfide

Solvothermal synthesis and characterization of cobalt sulfide nanocrystals

A new hydrothermal route for synthesis of molybdenum disulphide nanorods and related nanostructures

Modulating Crystallization of MoS 2 Nanostructures by Dimethyl Sulfoxide for Enhanced Hydrodesulfurization

Metastable MnS Crystallites Through Solvothermal Synthesis

Nanocrystalline Pyrite Cobalt Disulfide Synthesized by Solvent-thermal Preparation

A Novel One-Step Solvothermal Route to Nanocrystalline CuSbS2 and Ag3SbS3

CVD Synthesis of Intermediate State-Free, Large-Area and Continuous MoS2 via Single-Step Vapor-Phase Sulfurization of MoO2 Precursor

Monodisperse Cubic Pyrite NiS2 Dodecahedrons and Microspheres Synthesized by a Solvothermal Process in a Mixed Solvent: Thermal Stability and Magnetic Properties

Low-Temperature Synthesis of Near-Monodisperse Globular MoS2 Nanoparticles with Sulphur Powders

Hydrothermal Synthesis of Fine Mos2 Crystals from Na2moo4 and Kscn

A Simple Method for the Preparation of Nanocrystalline Transition Metal Sulfides