Abstract:Colloidal, monodisperse, single -crystalline pyramidal CuInS2 and rectangular AgInS2 nanocrystals were successfully synthesized through a convenient and improved solvothermal process that uses hexadecylamine as a capping reagent. The crystal phase, morphology, crystal lattice, and chemical composition of the as-prepared products were characterized by using X-ray diffraction, transmission electron microscopy (TEM), high-resolution TEM, and energy dispersive X-ray spectroscopy. Results revealed that the as-synthesized CuInS2 colloid is in the tetragonal phase (size: 13-17 nm) and the AgInS2 in the orthorhombic structure (size: 17 +/- 0.5nm). A possible shape evolution and crystal growth mechanism has been suggested for the formation of pyramidal CuInS2 and rectangular AgInS2 colloids. Control experiments indicated that the morphology- and/or phase-change of CuInS2 and orthorhombic AgInS2 colloids are temperature- and/or time-dependent. CuInS2 colloids absorb well in the range of visible light at room-temperature, indicating its potential application as a solar absorber. Two photoluminescence (PL) subbands at 1.938 and 2.384 eV in the PL spectra of CulnS(2) colloids revealed that the recombination of the closest and the second closest donor-acceptor pairs within the CuInS2 lattice, in which the donor defect (Cu) occupies an interstitial position and the acceptor defect (V-In) resides at an adjacent cation site. In addition, the synthesis strategy developed in this study is convenient and inexpensive, and could also be used as a general process for the synthesis of other pure or doped ternary chalcogenides that require a controlled size (or shape). This process could be extended to the synthesis of other functional nanomaterials.

Colloidal synthesis of monodisperse quaternary CuInSSe nanocrystals

A Redox Reaction to Synthesize Nanocrystalline Cu2-xSe in Aqueous Solution

Shape- and Phase-Controlled Synthesis of Monodisperse, Single-Crystalline Ternary Chalcogenide Colloids Through A Convenient Solution Synthesis Strategy

Formation of High-Quality I-Iii-Vi Semiconductor Nanocrystals by Tuning Relative Reactivity of Cationic Precursors

A new colloidal precursor cooperative conversion route to nanocrystalline quaternary copper sulfide

Colloidal Cu2ZnSnS4 nanocrystals generated by a facile route using ethylxanthate molecular precursors

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

Phase-Selective Synthesis and Self-Assembly of Monodisperse Copper Sulfide Nanocrystals

Facile synthesis and characterization of CuInS2 nanocrystals with different structures and shapes

Controllable Synthesis of Monodisperse CuS Nanocrystals

Controlled Synthesis of Luminescent Cuins2 Nanocrystals and Their Optical Properties

Size-, Shape-, and Assembly-Controlled Synthesis of Cu2−xSe Nanocrystalsvia a Non-Injection Phosphine-Free Colloidal Method

Non-Injection Synthesis of CuInS2/ZnS Nanocrystals and the Effect of Hydrophilic Surface Modification on Photoluminescence

Synthesis of High-Quality and Self-assembled Cu2ZnSnS4 Nanocrystals

Colloidosome-Based Synthesis Of A Multifunctional Nanostructure Of Silver And Hollow Iron Oxide Nanoparticles

General Synthesis of I-III-VI2 Ternary Semiconductor Nanocrystals.

Synthesis of Highly Monodisperse Cu2O Nanocrystals and Their Applications as Hole-Transporting Layers in Solution-Processed Light-Emitting Diodes.

Synthesis and Analysis of Zinc Copper Indium Sulfide Quantum Dot Nanoparticles

Colloidal Synthesis of Uniform CuI Nanoparticles and Their Size Dependent Optical Properties

A facile "dispersion-decomposition" route to metal sulfide nanocrystals

Solvothermal Synthesis and Characterization of Chalcopyrite CuInSe2 Nanoparticles