Abstract:A water-based route has been demonstrated for synthesizing ZnSe and Cd-doped ZnSe (ZnSe(ZnxCd1-xSe, 0 < x < 1) quantum dots (QDs) that have tunable and narrow photo luminescence (PL) peaks from the ultraviolet A (UVA) to the blue range (350-490 nm) with full-width at half-maximum (fwhm) values of 24-36 nm. Hydrazine (N2H4) was used to maintain oxygen-free conditions, allowing the reaction vessel to be open to air. The properties of the QDs were controlled using the thiol ligands, 3-mercaptopropionic acid (MPA), thiolglycolic acid (TGA), and L-glutathione (GSH). On the basis of optical spectra, linear three-carbon MPA attenuated nucleation and growth, yielding small ZnSe QDs with a high density of surface defects. In contrast, TGA and GSH produced larger ZnSe QDs with lower surface defect densities. The absorption spectra show that growth was more uniform and better controlled with linear two-carbon TGA than branched bifunctional GSH. After 20 min of growth TGA-capped ZnSe had an average diameter of 2.5 nm based on high-resolution transmission electron microscopy images; these nanocrystals had an absorbance peak maximum of approximately 340 nm (3.65 eV) and a band gap PL emission peak at 372 nm (3.34 eV). Highly fluorescent ZnxCd1-xSe QDs were fabricated by adding a Cd-thiol complex directly to ZnSe QD solutions; PL peaks were tuned in the blue range (400-490 nm) by changing the Zn to Cd ratio. The Cd-bearing nanocrystals contained proportionally more Se based on X-ray photoelectron spectroscopy, and Cd-Se bonds had ionic character, in contrast to primarily covalent Zn-Se bonds.

Synthesis and characterization of ZnSe and ZnSe/ZnS quantum dots for potential biomedical application

Controlled Synthesis and Characterization of Znse Quantum Dots

Synthesis and Characterization of Monodisperse CdSe Quantum Dots with Zinc Blende Structure

Photo-assisted synthesis of highly fluorescent ZnSe(S) quantum dots in aqueous solution

Zinc selenide quantum dots as fluorescent labels for biomedical imaging

Aqueous Synthesis of CdTe/CdS/ZnS Quantum Dots and Their Optical and Chemical Properties

Significant Improvement in Photoluminescence of ZnSe(S) Alloyed Quantum Dots Prepared in High Ph Solution

Synthesis and luminescence characteristics of DHLA-capped PbSe quantum dots with biocompatibility

Aqueous Synthesis and Fluorescence-Imaging Application of Cdte/Znse Core/Shell Quantum Dots with High Stability and Low Cytotoxicity

Preparation of water soluble CdSe and CdSe/CdS quantum dots and their uses in imaging of cell and blood capillary

Facile synthesis of water-soluble ZnS quantum dots with strong luminescent emission and biocompatibility

Synthesis of Sulfur-Selenium Doped Carbon Quantum Dots for Biological Imaging and Scavenging Reactive Oxygen Species

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

Fabrication of the CdSeTe Alloyed and CdSeTe/ZnS Core-Shell Quantum Dots

Preparation and Properties of High-quality CdSeS Alloyed Quantum Dots in Liquid Paraffin

Reaction-dependent optical behavior and theoretical perspectives of colloidal ZnSe quantum dots

Hydrothermal Synthesis of Mn-Doped Znse Quantum Dots and Effects of Surface Overcoating on Their Optical Properties

Semiconductor quantum dots: synthesis and water-solubilization for biomedical applications

Efficient, stable, small, and water-soluble doped ZnSe nanocrystal emitters as non-cadmium biomedical labels.

Synthesis And Characterization Of Water-Soluble Cdse/Cds/Zns Core-Shell Quantum Dots

Selenium quantum dots: Preparation, structure, and properties