Abstract:A water-based route has been demonstrated for synthesizing ZnSe and Cd-doped ZnSe (ZnSe(ZnxCd1-xSe, 0 < x < 1) quantum dots (QDs) that have tunable and narrow photo luminescence (PL) peaks from the ultraviolet A (UVA) to the blue range (350-490 nm) with full-width at half-maximum (fwhm) values of 24-36 nm. Hydrazine (N2H4) was used to maintain oxygen-free conditions, allowing the reaction vessel to be open to air. The properties of the QDs were controlled using the thiol ligands, 3-mercaptopropionic acid (MPA), thiolglycolic acid (TGA), and L-glutathione (GSH). On the basis of optical spectra, linear three-carbon MPA attenuated nucleation and growth, yielding small ZnSe QDs with a high density of surface defects. In contrast, TGA and GSH produced larger ZnSe QDs with lower surface defect densities. The absorption spectra show that growth was more uniform and better controlled with linear two-carbon TGA than branched bifunctional GSH. After 20 min of growth TGA-capped ZnSe had an average diameter of 2.5 nm based on high-resolution transmission electron microscopy images; these nanocrystals had an absorbance peak maximum of approximately 340 nm (3.65 eV) and a band gap PL emission peak at 372 nm (3.34 eV). Highly fluorescent ZnxCd1-xSe QDs were fabricated by adding a Cd-thiol complex directly to ZnSe QD solutions; PL peaks were tuned in the blue range (400-490 nm) by changing the Zn to Cd ratio. The Cd-bearing nanocrystals contained proportionally more Se based on X-ray photoelectron spectroscopy, and Cd-Se bonds had ionic character, in contrast to primarily covalent Zn-Se bonds.

Hydrothermal Synthesis of Mn-Doped Znse Quantum Dots and Effects of Surface Overcoating on Their Optical Properties

Microwave-Assisted Aqueous Synthesis of Transition Metal Ions Doped Znse/Zns Core/Shell Quantum Dots with Tunable White-Light Emission

Synthesis of Highly Emissive Mn-Doped ZnSe Nanocrystals without Pyrophoric Reagents

Optical Control of the Spindle-Liked ZnSe Quantum Dots with Precursor Solvent and Mn Doping

Near-infrared Colloidal Manganese Doped Quantum Dots: Photoluminescence mechanism and Temperature Response

Efficient and Color-Tunable Mn-Doped Znse Nanocrystal Emitters: Control of Optical Performance Via Greener Synthetic Chemistry

Enhanced luminescence using the core‐shell‐shell structure of 3‐mercaptopropionic acid‐capped ZnSe/ZnS: Mn/ZnS quantum dot

Highly Luminescent and Photostable Core/Shell/Shell ZnSeS/Cu:ZnS/ZnS Quantum Dots Prepared via a Mild Aqueous Route

Preparation of Manganese-Doped Znse Precursor Nanoribbon Bundles and Investigation of Its Magneto-Optical Properties

Facile synthesis, optical properties and growth mechanism of elongated Mn-doped ZnSe1-xSx nanocrystals

Reverse Micelles Synthesis And Optical Characterization Of Manganese Doped Cdse Quantum Dots

Facile Hydrothermal Synthesis of Mn Doped ZnS Nanocrystals and Luminescence Properties Investigations

Synthesis and Characterization of Monodisperse CdSe Quantum Dots with Zinc Blende Structure

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

The Design of Mn2+&Co2+ Co-Doped CdTe Quantum Dot Sensitized Solar Cells with Much Higher Efficiency.

Efficient, stable, small, and water-soluble doped ZnSe nanocrystal emitters as non-cadmium biomedical labels.

Aqueous synthesis of Cu-doped ZnCdS/ZnS core/shell nanocrystals with a new and highly reactive sulfur source

Enhanced Photoluminescence and Characterization of Mn-Doped Zns Nanocrystallites Synthesized in Microemulsion

Colloidal manganese doped ZnS nanoplatelets and their optical properties

Quantum Confinement Effect and Photoenhancement of Photoluminescence of PbS and PbS/MnS Quantum Dots

Temperature- And Mn2+ Concentration-Dependent Emission Properties Of Mn2+-Doped Znse Nanocrystals