Magnetically Recoverable Ni@C Composites: the Synthesis by Carbonization and Adsorption for Fe3+

Xiaowen Wu,Zhijie Zhang,Chao Xia,Biqiong Chen,Xiaozhao Jin,Zhaohui Huang,Yan-gai Liu,Minghao Fang,Xin Min

DOI: https://doi.org/10.1016/j.jallcom.2017.05.029

IF: 6.2

2017-01-01

Journal of Alloys and Compounds

Abstract:Carbon-encapsulated nickel particles (Ni@C composites) for removing Fe3+ in wastewater have been prepared by the carbonization of phenolic resin mixing with nickel particles. XRD results reveal that the Ni@C composites are consisted of C, Ni, and Ni3S2. The TG-DTG curves of Ni@C composites are almost same as that of phenolic resin. The morphology investigation shows that Ni is distributed randomly on carbon. Based on analysis of N-2 adsorption-desorption isotherm, the surface area and pore volume of Ni@C composites are 187.47 m(2) g(-1) and 0.06900 cm(3) g(-1) nm(-1), respectively. The saturation magnetization values for Ni@C composites are 68.99 emu.g(-1) determined by the Vibrating Sample Magne-tometer. Ni@C composites exhibit a high adsorption capacity for Fe3+. The adsorption behavior follows the pseudo-second-order kinetic and Langmuir model between the adsorbents and Fe3+. Furthermore, the adsorption capacity of Ni@C composites derives from the attractive force between the adsorbed anion and the surface positive charge of Ni@C composites, as well as the bond between the adsorbed cation and the COO- groups. From the above results Ni@C composites can be widely applied in wastewater treatment as a new efficiency and excellent recoverable adsorbent. (C) 2017 Elsevier B.V. All rights reserved.