Phase evolution and microwave dielectric properties of the Li 2(1+ x ) ZnGe 3 O 8 spinel oxides

Weishuang Fang,Laiyuan Ao,Ying Tang,Jie Li,Huaicheng Xiang,Zhiwei Zhang,Qianbiao Du,Liang Fang

DOI: https://doi.org/10.1007/s10854-020-03904-8

2020-01-01

Abstract:Recently, there have been considerable interests in the Li-containing spinel oxides as promising microwave dielectric materials. Li loss at elevated temperatures, however, is known to be inevitable, resulting in deterioration on dielectric performances. Here the influence of Li nonstoichiometry on the microwave dielectric properties of Li 2 ZnGe 3 O 8 , a spinel oxide, was reported. An appropriate level of Li excess enhanced the densification of Li 2 ZnGe 3 O 8 and increased dielectric performances. In contrast, high level of Li excess induced the formation of the secondary phase of Li 2 ZnGeO 4 confirmed by XRD and Raman spectra, which in turn lowered the dielectric properties. Typically, a composition with x = 0.075, in the Li 2(1+ x ) ZnGe 3 O 8 ceramics exhibited the enhanced microwave dielectric properties with ε r = 10.68, Q × f = 77,300 GHz (at 13.3 GHz), and τ f = − 70.35 ppm/°C when sintered at 940 °C for 4 h. Moreover, these compounds have well chemical compatibility with the silver electrodes.