Influence of (Zn0.5Ti0.5)3+substitution on structural evolution, bond characteristics, and microwave dielectric properties of spinel Li (Zn0.5Ti0.5)xGa5-xO8 solid solutions

Jun Yang,Laiyuan Ao,Xiaofang Luo,Chuanqing Chen,Xing Zhang,Liang Fang,Bin Tang,Xianzhong Tang

DOI: https://doi.org/10.1016/j.ceramint.2023.06.037

IF: 5.532

2023-01-01

Ceramics International

Abstract:In this study, the evolution of phase and bond characteristics, as well as the consequent effects on the microwave dielectric properties of Li(Zn0.5Ti0.5)xGa5-xO8 ceramics were investigated. XRD and Rietveld refinement patterns revealed that the sample underwent a transformation from a low-symmetry inverse cubic spinel phase, characterized by the P4332 space group, to a high-symmetry cubic spinel phase associated with the Fd-3m space group. All samples displayed compact grain structures in their surface micro-morphologies, and they achieved high relative densities exceeding 97% when sintered at their respective optimal temperatures. With increasing x value, the dielectric constant increases due to the growth in ionicity and atheo/Vm. Concurrently, the zf value shifts from -69.29 ppm/degrees C to -48.73 ppm/degrees C, a trend that aligns with the bond valence changes at the octahedral position as a function of x. In the range of 0 < x < 3, the Q x f value initially increased due to the change in symmetry, growth in lattice energy, and reduction of Ti3+ content. However, it subsequently decreased as a result of further disruption in ordering and diminishing lattice energy. The optimal microwave dielectric properties were obtained for the x = 3 sample (LiZn1.5Ti1.5Ga2O8) sintered at 1220 degrees C, displaying characteristics of er = 16.46, Q x f = 79,268 GHz and zf = -53.36 ppm/degrees C.