Cation distribution and bond energy of intermediate spinel Mg (Zn<sub>0.5</sub>Ti<sub>0.5</sub>)<sub>2x</sub>Ga(<sub>2-2x</sub>)O<sub> 4</sub> microwave dielectric ceramics

Shiyao Shen,Ying Tang,Jie Li,Weishuang Fang,LaiYuan Ao,Xiangguang Zhao,Liang Fang
DOI: https://doi.org/10.1016/j.ceramint.2021.08.283
IF: 5.532
2021-01-01
Ceramics International
Abstract:Substitution of Ga3+ by [Zn0.5Ti0.5]3+ in MgGa2O4 improved the comprehensive properties of the resultant spinel. A continuous solid solution with a spinel structure was formed in Mg(Zn0.5Ti0.5)2xGa(2- 2x)O4 (0 < x < 1); here, Zn2+ occupied the tetrahedral 8a site while Ti4+ occupied the octahedral 16d site, resulting in a decrease in the degree of inversion lambda from 0.86 to 0. The optimal sintering temperature decreased from 1460 degrees C to 1220 degrees C, and the dielectric constant (epsilon r) increased from 8.8 to 14.9; these changes could be ascribed to the greater polarizability of [Zn0.5Ti0.5]3+ relative to that of Ga3+. The temperature coefficient of resonant frequency (tau f) of the material remarkably increased from -64.1 ppm/degrees C to -16.8 ppm/degrees C, which may be attributed to the increase in dielectric polarizability/molecular volume, bond energy, and bond valence in B-sites. The high-quality factor (Q x f) slightly decreased from 89,253 GHz to 73,432 GHz with decreasing lambda and packing fraction. Optimal microwave dielectric properties were obtained from the sample with x = 1 and sample sintered at 1220 degrees C; in this case, epsilon r = 14.9, Q x f = 73,432 GHz, and tau f = -16.8 ppm/degrees C.
What problem does this paper attempt to address?