Phase evolution, far-infrared spectra, and ultralow loss microwave dielectric ceramic of Zn 2 Ge 1+ x O 4+2 x (− 0.1 ≤ x ≤ 0.2)

Changzhi Yin,Ying Tang,Junqi Chen,Chunchun Li,Liang Fang,Feihu Li,Yijun Huang

DOI: https://doi.org/10.1007/s10854-019-02044-y

2019-01-01

Abstract:A series of willemite based ceramics Zn 2 Ge 1+ x O 4+2 x with − 0.1 ≤ x ≤ 0.2 were prepared by the solid-state reaction method. Influences of Ge nonstoichiometry on the crystal structure, densification, and microwave dielectric properties were evaluated in terms of X-ray diffraction, SEM, dielectric measurements and far-infrared spectra. Ge excess favored the formation of single-phase willemite but a high level of excess induced appearance of GeO 2 . In contrast, nominal composition and those with Ge deficiency comprised of ZnO and the willemite phase. Ge excess was found to be beneficial to the densification and dielectric properties optimization of Zn 2 Ge 1+ x O 4+2 x . A composition with x = 0.1 (Zn 2 Ge 1.1 O 4.2 ) exhibited the optimum microwave dielectric properties with a relative permittivity ε r ~ 7.09, a quality factor Q × f ~ 112,700 GHz (at 14.48 GHz), and a temperature coefficient of resonance frequency τ f ~ − 51 ppm/°C.