Phase evolution, structure and microwave dielectric properties of Li2+xMg3SnO6 (x = 0.00–0.12) ceramics

Zixuan Fang,Bin Tang,Feng Si,Enzhu Li,Hongyu Yang,Shuren Zhang

DOI: https://doi.org/10.1016/j.ceramint.2017.07.074

IF: 5.532

2017-01-01

Ceramics International

Abstract:In this study, the Li2+xMg3SnO6 (LxMS) ceramic systems were prepared by solid-state reaction using novel atmosphere-controlled sintering (x = 0.00–0.12). The influences of extra lithium contents on the phase evolution, crystal structure and microwave dielectric properties of Li2+xMg3SnO6 (LxMS) ceramics were systematically investigated. As samples were calcined from 800 to 1000°C, the Li2Mg3SnO6 phase was formed from the chemical reaction between Li2SnO3 and MgO phase. Pure Li2Mg3SnO6 phase could be observed for samples calcined at 1000–1100°C. But when it was exposed to high temperature air over 1100°C, the Li2Mg3SnO6 decomposed into Mg2SnO4, MgO and Li2O. Because of the protective atmosphere and extra lithium, the εr, Q×f and τf were significantly improved by the suppression of secondary phase and pores for 0.00≤x≤0.08. However, comprehensive microwave characteristics were deteriorated for 0.08<x≤0.12, which were correlated with dielectric polarization, bond valence, FWHM, packing fraction and octahedral distortion. The excellent microwave characteristics of LxMS (x = 0.08) sintered at 1350°C in novel controlled atmosphere were obtained: εr = 12.7, Q×f = 168,330GHz and τf = −27.4ppm/°C.