Abstract:MgO ceramics show good microwave dielectric properties, but their high sintering temperature limits the practical applications. LiF is an ideal sintering aid (melting point of 848 °C) and does not easily react with MgO to form any secondary phase. Herein, MgO-xwt%LiF ceramics (x = 2–10, with a step of 2) with ultralow loss were fabricated using a conventional solid-state process. The X-ray diffraction and Rietveld refinement results revealed that the lattice parameters and unit cell volume of the ceramics first increased and then decreased with LiF content increase. The compositions of the ceramics were analyzed using energy-dispersive X-ray spectroscopy, and superfluous LiF appeared whenx≥4. Notably, at x = 4 and T = 950 °C, the grain distribution was dense and uniform, and the quality factor of the MgO-xwt%LiF ceramics reached the maximum value of 120288 GHz (at 12 GHz), and the other properties also attained the optimal level: εr = 9.66 and τf = -20.66 ppm/°C. Meanwhile, the dielectric properties of the ceramics were studied over a broad frequency range (up to the terahertz frequencies). The ceramics showed excellent dielectric properties, such as a low dielectric constant of 9.252 (at 1 THz) and a low dissipation factor tanδ of 0.0058. In summary, the MgO ceramics were not only found to be suitable for application in the microwave range, but also showed huge potential for application value in the terahertz frequency range.

Series of Thermally Stable Li1+2xMg4−xV3O12 Ceramics: Low Temperature Sintering Characteristic, Crystal Structure and Microwave Dielectric Properties

A Novel Thermally Stable Low-Firing Limg4v3o12 Ceramic: Sintering Characteristic, Crystal Structure and Microwave Dielectric Properties

Temperature Stable Microwave Dielectric Ceramics in LiCa 3− X Sr X MgV 3 O 12 Ceramics

Temperature Stability and High-Qf of Low Temperature Firing Mg2SiO4–Li2TiO3 Microwave Dielectric Ceramics

Temperature Stable and Low Loss Microwave Dielectric Ceramics of Li2Mg3-xSrxTiO6

Influence of Low Concentration Mgco2(Vo4)(2) Addition on Microwave Dielectric Properties of Ba0.6sr0.4tio3 Ceramics

Low temperature sintered Li6MgTiNb1-xVxO8F microwave dielectric ceramics with high-quality factor

Sintering Characteristics and Microwave Dielectric Properties of Low-Temperature-fired (1–x)li3mg2nbo6–xli2wo4 Ceramics

Crystal Structure and Microwave Dielectric Properties of Li2(Mg1–xCux)2Mo3O12 Ceramics Sintered at Ultra‐low Temperature

Effect of Mn:Mg ratio on Sintering Behavior and Microwave Dielectric Properties of (Mn, Mg)V 2 O 6 Ceramics at Ultra-low Sintering Temperature

Correlations between the structural characteristics and enhanced microwave dielectric properties of V–modified Li3Mg2NbO6 ceramics

Microwave dielectric properties of LiMVO 4 (M=Mg, Zn) ceramics with low sintering temperatures

Novel temperature stable Li 2 TiO 3 -based microwave dielectric ceramics with low loss

A low εr and temperature-stable Li3Mg2SbO6 microwave dielectric ceramics

Relationship Between Structure and Properties of Microwave Dielectric Ceramic Li(1+x)2MgTi3O8 Based on Li Non-Stoichiometry

Temperature Stable and High-Q Microwave Dielectric Ceramics in the Li2Mg3−Ca TiO6 System (X=0.00–0.18)

Glass-free CaMg0.9−xLi0.2MnxSi2O6 ceramics with enhanced dielectric properties for microwave and THz frequency applications

High-quality Factor of (1 − X) Li2Mg3TiO6-xBaV2O6 (x = 0.1, 0.3, 0.4, 0.5, 0.6) Ceramics with Low Sintering Temperature

Enhanced microstructure and dielectric properties of low-temperature sintered MgO-xwt%LiF ceramics for high-frequency applications

Low-temperature sintering and microwave dielectric properties of CaMg1−xLi2xSi2O6 (x = 0−0.3) ceramics

Low-temperature sintering and microwave dielectric properties of CaMg 1− x Li 2 x Si 2 O 6 ( x = 0−0.3) ceramics