Abstract:Li2SiO3 ceramic is one of the most important candidate materials for high-frequency microwave ceramics; however, minimal information about the relationship between the structure and microwave dielectric properties of non-stoichiometric Li2+xSiO3 ceramics is available. In the present work, nominal Li2+xSiO3 (x=0, 0.04, 0.08, 0.12 and 0.16) ceramics were prepared by a conventional solid-state sintering technique. The structure of Li2+xSiO3 ceramics was investigated via X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM) as well as Raman spectra experiment and calculation. Refinements showed that part of the non-stoichiometric Li ions entered the Li2SiO3 lattice. Along with the results of the XRD analysis, Raman spectra experiment and calculation confirmed the presence of Li2Si2O5 phase in all the samples. Compared with stoichiometric Li2SiO3, non-stoichiometric Li provided higher densification and less ordering. Moreover, the SiO4 tetrahedrons formed more ionic bonds, which reduced distortion polarization. Further, the dielectric constants, which were observed to be mainly dependent on distortion polarization and densification, firstly increased then decreased slightly with increasing non-stoichiometric Li content. However, the quality factor (Q×f), which was primarily driven by ordering degree of Li-O bonds, firstly decreased then increased with increasing non-stoichiometric Li content. The results obtained on the Li2+xSiO3 ceramics, might offer some useful information for study and application about high-frequency microwave.

Study on properties of nonstoichiometric Li(2+x)ZnTi3O(8+0.5x) microwave dielectric ceramics

Effect of TiO 2 Ratio on the Phase and Microwave Dielectric Properties of Li 2 ZnTi 3+ x O 8+2 x Ceramics

Microwave dielectric properties of temperature stable Li2ZnxCo1−xTi3O8 ceramics

Temperature Stability of Li2TiO3‐Zn2SiO4 Microwave Dielectric Ceramics

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Effects of Li 2 ZnTi 3 O 8 Addition on Sintering Behavior and Microwave Dielectric Properties of the MgTiO 3 –catio 3 Ceramic System

Investigation of the microwave dielectric properties of the Li4x/3Zn2−2xTi1+2x/3O4 system by P–V–L theory and vibration spectroscopy

Phase Structure and Microwave Dielectric Properties of (1−x)li2zn3ti4o12−xtio2 Ceramics

Effect of Phase, Chemical Bond and Vibration Characteristics on the Microwave Dielectric Properties of Temperature-Stable Zn1−x(Li0.5Bi0.5)xMoxW1−xO4 Ceramics

Microwave Dielectric Properties and Low Temperature Firing of (1 − X)li2zn3ti4o12 –xli2tio3 (0.2 ≤ X ≤ 0.8) Ceramics with B2O3–CuO Addition

Relationship Between Structure and Properties of Microwave Dielectric Ceramic Li(1+x)2MgTi3O8 Based on Li Non-Stoichiometry

Li+ enrichment to improve the microwave dielectric properties of Li2ZnTi3O8 ceramics and the relationship between structure and properties

The effect of composition on Li2(Mg0.3Zn 0.7)Ti3O8-xTiO2 microwave dielectric ceramics for low temperature co-fired ceramics technology application

Microwave Dielectric Properties and Low-Temperature Sintering of (zn0.8mg0.2)2sio4–tio2 Ceramics with Li2O–B2O3

Novel temperature stable Li 2 TiO 3 -based microwave dielectric ceramics with low loss

Enhancement of the Cation Order and the Microwave Dielectric Properties of Li2ZnTi3O8 Through Composition Modulation

Effects of Cu Substitution on Microstructures and Microwave Dielectric Properties of Li2ZnSiO4 Ceramics

Relationship Between the Structure and Microwave Dielectric Properties of Non-Stoichiometric Li2+xSiO3 Ceramics

Microwave Dielectric Properties and Low Temperature Sintering of Li 2 Zn(Ti 1−x Sn X ) 3 O 8 (x ≤ 0.20) Ceramics with B 2 O 3 –cuo Addition

Effects of Cu2+substitution on bond characteristics, Raman spectra, and microwave dielectric properties of Li2Mg0.6Zn0.4SiO4 ceramics

Microwave Dielectric Properties in the Li4+Ti5O12 (0 ≤ X ≤ 1.2) Ceramics