Effect of TiO 2 Ratio on the Phase and Microwave Dielectric Properties of Li 2 ZnTi 3+ x O 8+2 x Ceramics

Yingxiang Li,Hao Li,Junshan Li,Bin Tang,Shuren Zhang,Hetuo Chen,Ya Wei

DOI: https://doi.org/10.1007/s11664-014-3026-4

IF: 2.1

2014-01-01

Journal of Electronic Materials

Abstract:Low-loss materials Li 2 ZnTi 3+ x O 8+2 x (LZT) ( x = 0, 0.10, 0.17, 0.25, 1.00) were prepared by the conventional solid-state route. The effect of TiO 2 ratio on phase composition, microstructure, and the microwave dielectric properties of Li 2 ZnTi 3+ x O 8+2 x ceramics were investigated using x-ray diffraction, scanning electron microscopy, energy-dispersive x-ray spectroscopy, and Vector Network Analyzer. The results revealed that a two-phase system Li 2 ZnTi 3 O 8 -TiO 2 was formed. The appropriate content of TiO 2 ratio can effectively adjust the temperature coefficient of the resonant frequency ( τ f ) value from −14.5 to 0 ppm/ °C without obvious degradation of the microwave dielectric properties. The microwave dielectric properties of the Li 2 ZnTi 3+ x O 8+2 x materials were characterized at microwave frequencies. Typically, the Li 2 ZnTi 3+ x O 8+2 x ( x = 0.17) ceramic sintered at 1,160 °C for 5 h showed excellent microwave dielectric properties with ε r = 28.51, Q × f = 58,511 GHz, and τ f = + 2.3 ppm/ °C.