Phase structure and microwave dielectric properties of Zr(Zn 1/3 Nb 2/3 ) x Ti 2−x O 6 (0.2 ≤ x ≤ 0.8) ceramics

Bin Tang,Shengquan Yu,Hetuo Chen,Shuren Zhang,Xiaohua Zhou

DOI: https://doi.org/10.1007/s10854-012-0955-7

2012-01-01

Abstract:The phase structure, morphology and microwave dielectric properties of Zr(Zn 1/3 Nb 2/3 ) x Ti 2−x O 6 (0.2 ≤ x ≤ 0.8) ceramics were investigated as a function of the amount of (Zn 1/3 Nb 2/3 ) 4+ substitution by the solid-state reaction technique. X-ray diffraction analysis showed the co-existence of the solid solution ZrTiO 4 (x = 0.2) or ZrTi 2 O 6 (x = 0.4–0.5) as the main phase and TiO 2 as the second phase, and the single-phase region for substituted ZrTi 2 O 6 was obtained with x ≥ 0.5. As increasing x from 0.2 to 0.8, the grain growth was promoted, moreover the dielectric constant ε r and the temperature coefficient of resonant frequency τ f dropped from 53.8 to 39.2 and from +106.2 to −25.5 ppm/°C respectively, and the Q × f values increased from 33,200 to 43,200 GHz. Ceramics with good microwave dielectric properties: ε r = 41.7, Q × f = 42,100 GHz and τ f = −15.5 ppm/°C was obtained at x = 0.6.